Electrochromic elements, materials for use in such element, processes for making such elements and such materials and use of such element in an electrochromic glass device

• US 5,086,351 A
• Filed: 07/13/1989
• Issued: 02/04/1992
• Est. Priority Date: 07/13/1989
• Status: Expired due to Term

• Current Assignee: Arkema Incorporated (Arkema), Societe Nationale Elf Aquitaine (Cook Composites and Polymers)
• Original Assignee: Societe Nationale Elf Aquitaine (Cook Composites and Polymers), M&T Chemicals Incorporated
• Inventors: Couput, Jean Paul, Campet, Guy
• Primary Examiner(s): Laroche, Eugene R.
• Assistant Examiner(s): Shingleton, Michael B.
• Application Number:
  US07/379,225
• Time in Patent Office: 936 Days
• Field of Search: 350/357, 429/192, 252/62.2, 204/192.1, 427/126.1, 427/164
• US Class Current: 359/265
• CPC Class Codes: G02F 1/1524 Transition metal compounds
• CPC Class Codes: G02F 1/1525 characterised by a particular ion transporting layer, e.g. electrolyte

Abstract

An electrochromic element useful in an electrochromic glass or mirror device and a process for making such element. The element is a five-layered structure including an electrolyte ion conducting layer interposed between first and second inorganic electrochromic layers which are interposed between a pair of conductive electrodes. The first and second inorganic electrochromic layers are different and are capable of exhibiting color-forming properties complementary to one another upon the incorporation of an alkali metal or Ag ion, a mixture of alkali metal or Ag ions or a mixture of alkali metal or Ag and hydrogen ions. The electrolyte ion conducting layer may be a copolymer of ethylene oxide, butylene oxide or methyl glycidyl ether, and optionally a small amount of allyl glycidyl ether, along with an ionizable salt, or may be a polyurethane gel forming by reacting the copolymer with triisocyanate, along with an ionizable salt. The second inorganic electrochromic layer comprises a transition metal oxide which exhibits a color change when shifting between the +2 and +3 valence states. The second inorganic electrochromic layer may be produced by an electrochemical process, a chemical process, or by a physical process. The electrochromic element may also comprise a plurality of five-layer structure in tandem, each pair separated by a substrate.

Claims

1. An electrochromic element comprising a pair of conductive electrodes at least one of which is transparent, first and second inorganic electrochromic layers interposed between said pair of conductive electrodes and an ion conducting layer of an electrolyte interposed between said first and second inorganic electrochromic layers, wherein said first and second inorganic electrochromic layers are different and are capable of exhibiting electrochromic properties upon the incorporation of an alkali metal or Ag ion, wherein the electrochromic properties of said first and second inorganic electrochromic layers are complementary, and wherein said second inorganic electrochromic layer comprises the composition

View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25)

2. The element of claim 1 wherein said second inorganic electrochromic layer is formed by sputtering a target of transition metal T with an O₂ /H₂ plasma to form an original layer consisting essentially of a mixture of TO, T(OH)₂ and TOOH;

electrochemically processing the original layer in a basic solution to form a formated layer consisting essentially of TO and TOOH; and

electrochemically processing the formated layer consisting essentially of TO and TOOH in a liquid electrolyte comprising a polar solvent and an ionizable salt of a strong acid and a member selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals and a mixture of at least one alkali metal with Ag, to form said second inorganic electrochromic layer having the composition M_x+y T^II_1-2x+y T^III_x-y O.

3. The element of claim 1 wherein said second inorganic electrochromic layer is formed by sputtering a target of M.sub.α

T_1-α

O, wherein O<

α

<

1.0, to form a thin film of M_m T_n^II T_p^III O, m,n and p being mole fractions, and electrochemically processing the thin film in a liquid electrolyte comprising a polar solvent and an ionizable salt of a strong acid and a member selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals and a mixture of at least one alkali metal with Ag, to form said second inorganic electrochromic layer having the composition M_x+y T^II_1-2x+y T^III_x-y O.

4. The element of claim 1, wherein said yM⁺ ions can be inserted into said second inorganic electrochromic layer by applying a voltage differential between said pair of conductive electrodes.

5. The element of claim 1, wherein T is selected from Ni, Co, Mn and Fe.

6. The element of claim 1, wherein M is Li.

7. An electrochromic mirror device comprising the electrochromic element of claim 1 interposed between a pair of substrates, wherein one of the conductive electrodes is reflective and the other is transparent.

8. An electrochromic device comprising a plurality of electrochromic elements as recited in claim 1 in juxtaposed surface to surface relation, wherein a transparent substrate is interposed between each pair of electrochromic elements and the plurality of electrochromic elements are interposed between a pair of transparent substrates.

9. The element of claim 1, wherein said ion conducting layer of a solid polymeric electrolyte is a solid solution of an ionizable salt in a polymer capable of conducting an amount of alkali metal or silver ions between said first and second inorganic electrochromic layers sufficient to cause each of said first and second inorganic electrochromic layers to exhibit a complementary color change, with said ion conducting layer remaining amorphous and transparent.

10. The element of claim 9, wherein said first inorganic electrochromic layer is MoO₃.

11. The element of claim 9, wherein said first inorganic electrochromic layer is CrO₂.

12. The element of claim 9, wherein said ion conducting layer of a solid polymeric electrolyte comprises a copolymer of ethylene oxide and methyl glycidyl ether and at least one ionizable salt.

13. The element of claim 9, wherein said ion conducting layer of a solid polymeric electrolyte comprises a copolymer of ethylene oxide and butylene oxide and at least one ionizable salt.

14. The element of claim 9, wherein said ion conducting layer of a solid polymeric electrolyte comprises:

a polyurethane gel formed by reacting a triisocyanate with a copolymer of ethylene oxide and butylene oxide having a molecular weight ranging between 1,000 and 20,000; and

at least one ionizable salt.

15. The element of claim 9, wherein said ion conducting layer of a solid polymeric electrolyte comprises:

a polyurethane gel formed by reacting a triisocyanate with a copolymer of ethylene oxide and methyl glycidyl ether having a molecular weight ranging between 1,000 and 20,000; and

at least one ionizable salt.

16. The element of claim 9, wherein said first inorganic electrochromic layer is WO₃.

17. The element of claim 16, wherein said pair of conductive electrodes are fluorine doped tin oxide (SNO₂ :

F).

18. The element of claim 16, wherein said pair of conductive electrodes are indium-tin oxide.

19. An electrochromic device comprising the element of claim 18 interposed between a pair of transparent substrates.

20. The electrochromic device of claim 19, wherein said pair of transparent substrates are glass.

21. The electrochromic device of claim 19, wherein said pair of transparent substrates are plastic.

22. A method of manufacturing the device of claim 19, comprising:

sputtering a layer of a conductive electrode material on a first substrate;

sputtering a layer of a first inorganic electrochromic material onto said conductive electrode layer on said first substrate;

sputtering a layer of a conductive electrode material on a second substrate;

sputtering a layer of a second inorganic electrochromic material onto said conductive electrode layer on said second substrate; and

assembling an ion conducting layer of a solid polymeric electrolyte between the sputtered sides of said first and second substrates.

23. The element of claim 16, wherein M⁺ ions are capable of being inserted from said ion conducting layer to said first inorganic electrochromic layer to form the composition

MWO₃, which is cooled.

24. The element of claim 23, capable of exhibiting

(a) a first color state when y=x wherein said second inorganic layer is bleached and has the composition MT^II O and said first inorganic layer is bleached and has the composition WO₃, and

(b) a second color state when y<

x wherein said second inorganic layer is colored and has the composition MT^II T^III O and said first inorganic layer is colored and has the composition MWO₃,

said first color state having a first transmissivity and said second color state having a transmissivity less than said first transmissivity.

25. The element of claim 23, wherein said M⁺ ions can be inserted into said first inorganic electrochromic layer by applying a voltage differential between said pair of conductive electrodes.

26. An electrochromic element comprising the following layers, in order:

a first transparent conductive electrode;

a first inorganic electrochromic layer;

a first ion conducting layer of an electrolyte;

a first inorganic electrochromic counter electrode layer;

a second transparent conductive electrode, a transparent substrate;

a third transparent conductive electrode;

a second inorganic electrochromic counter-electrode layer;

a second ion conducting layer of an electrolyte;

a second inorganic electrochromic layer and a fourth conductive electrode which may be transparent or reflective;

wherein said first and second inorganic electrochromic layers are different from said first and second inorganic electrochromic counter electrode layers;

said first and second inorganic electrochromic layers and said first and second inorganic electrochromic counter electrode layers are capable of exhibiting electrochromic properties upon the incorporation of an alkali metal or Ag ion, a mixture of alkali metal or Ag and hydrogen ions, or a mixture of alkali metal or Ag ions;

wherein the electrochromic properties of said first and second inorganic electrochromic layers are complementary to the electrochromic properties of said first and second inorganic electrochromic counter electrode layers, and wherein at least one of said first and second inorganic electrochromic counter electrode layers comprises the composition

space="preserve" listing-type="equation">M.sub.x+y T.sup.II.sub.1-2x+y T.sup.III.sub.x-y O,

wherein T^II and T^III are divalent and trivalent forms of a transition metal T;

M is selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals, a mixture of at least one alkali metal and Ag, a mixture of Ag and hydrogen, a mixture of at least one alkali metal and hydrogen and a mixture of at least one alkali metal with Ag and hydrogen;

x is a first mole fraction of M⁺ ions and y is a second mole fraction of M⁺ ions incorporated into said first and second inorganic electrochromic counter electrode layers such that 0<

x≦

1.0, -x≦

y≦

+x and y≧

2x-1; and

wherein the composition undergoes a maximum transmissivity change when y varies between -x and +x.

27. An electrochromic device comprising the element of claim 26 interposed between a pair of transparent substrates.

28. A method of manufacturing the device of claim 27, comprising:

sputtering a layer of a conductive electrode material on a first substrate;

sputtering a layer of a first inorganic electrochromic material onto said conductive electrode layer on said first substrate;

sputtering a layer of a conductive electrode material on a second substrate;

sputtering a layer of a first inorganic electrochromic material onto said conductive electrode layer on said second substrate;

sputtering a layer of a conductive electrode material on each side of a third substrate;

sputtering a layer of a second inorganic electrochromic material on said conductive electrode layers on each side of said third substrate;

assembling the sputtered side of said first substrate into juxtaposed contact with one side of said third substrate with an ion conducting layer of solid polymeric electrolyte interposed therebetween; and

assembling the sputtered side of said second substrate into juxtaposed contact with the other side of said third substrate with an ion conducting layer of a solid polymeric electrolyte interposed therebetween.

29. An electrochromic material having the formula:

M_x+y T^II_1-2x+y T^III_x-y O, wherein M is selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals, a mixture of at least one alkali metal and Ag, a mixture of Ag and hydrogen, a mixture of at least one alkali metal and hydrogen and a mixture of at least one alkali metal with Ag and hydrogen;

T^II and T^III are divalent and trivalent forms of a transition metal T;

x is a first mole fraction of M⁺ ions and y is a second mole fraction of M⁺ ions incorporated into the electrochromic material such that O<

x≦

1.0, -x<

y<

+x and y>

2x-1; and

wherein said electrochromic material undergoes a maximum transmissivity change when y varies between -x and +x.

30. The electrochromic material of claim 29, wherein M is Li.

31. The electrochromic material of claim 29, wherein T is selected from Ni, Co, Mn and Fe.

32. A process for producing an electrochromic material comprising:

a first step of forming an original thin film consisting essentially of a mixture of TO, T(OH)₂ and TOOH by sputtering a target comprising T with an O₂ /H₂ plasma;

a second step of electrochemically processing the original thin film in a basic solution to give a layer consisting essentially of TO and TOOH;

a third step of electrochemically processing the layer consisting essentially of TO and TOOH in a liquid electrolyte comprising a polar solvent and an ionizable salt of a strong acid and a member selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals and a mixture of at least one alkali metal with Ag, to incorporate (x+y) cations from the ionizable salt into the layer consisting essentially of TO and TOOH to form an electrochromic material having the composition M_x+y T^II_1-2x+y T^III_x-y O;

wherein T is a transition metal selected from Ni, Co, Mn and Fe;

M is selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals, a mixture of at least one alkali metal and Ag, a mixture of Ag and hydrogen, a mixture of at least one alkali metal and hydrogen and a mixture of at least one alkali metal with Ag and hydrogen;

T^II and T^III are divalent and trivalent forms of transition metal T and x and y are mole fractions such that 0<

x≦

1.0, -x≦

y≦

x and y≧

2x-1.

33. A process for producing an electrochromic material comprising:

a first step of sputtering a target of M.sub.α

T_1-α

O, wherein O<

α

≦

1.0, to form a thin film of M_m T_n^II T_p^III O, m, n and p being mole fractions;

a second step of electrochemically processing the thin film in a liquid electrolyte comprising a polar solvent and an ionizable salt of a strong acid and a member selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals and a mixture of at least one alkali metal with Ag, to incorporate (x+y) cations from the ionizable salt into the thin film to form an electrochromic material having the composition M_x+y T^II_1-2x+y T^III_x-y O;

wherein T is a transition metal selected from Ni, Co, Mn and Fe;

T^II and T^III are divalent and trivalent forms of transition metal T;

M is selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals, and a mixture of at least one alkali metal and Ag; and

x and y are mole fractions such that 0<

x≦

1.0, -x≦

y≦

x and y≧

2x-1.

34. An electrochromic material having the formula M_x+y T^II_1-2x+y T^III_x-y O, wherein T^II and T^III are divalent and trivalent forms of a transition metal T;

M is selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals and a mixture of at least one alkali metal and Ag;

x and y are a first mole fraction and a second mole fraction of M⁺ ions incorporated into the electrochromic material such that 0<

x≦

1.0, -x<

y<

x and y<

2x-1; and

wherein said electrochromic material undergoes a maximum transmissivity change when y varies between -x and +x.

35. The electrochromic material of claim 34, wherein the transition metal T is selected from the group consisting of Ni, Co, Mn and Fe.

36. An electrochromic element comprising a pair of conductive electrodes at least one of which is transparent, first and second inorganic electrochromic layers interposed between said pair of conductive electrodes and an ion conducting layer of an electrolyte interposed between said first and second inorganic electrochromic layers, wherein said first and second inorganic electrochromic layers are different and are capable of exhibiting electrochromic properties upon the incorporation of an alkali metal or Ag ion, wherein the electrochromic properties of said first and second inorganic electrochromic layers are complementary and wherein the second inorganic electrochromic layer comprises an electrochromic material having the formula M_x+y T^II_1-2x+y T^III_x-y O, wherein T^II and T^III are divalent and trivalent forms of a transition metal T, M is selected from the group consisting of an alkali metal, Ag, a mixture of alkali metals and a mixture of at least one alkali metal and Ag, x and y are a first mole fraction and a second mole fraction of M⁺ ions incorporated into the electrochromic material such that 0<

x<

1.0, -x≦

y≦

x and y≧

2x-1, said electrochromic material undergoing a maximum transmissivity change when y varies between -x and +x.