Process of manufacturing cast tungsten carbide spheres

• US 5,089,182 A
• Filed: 10/16/1989
• Issued: 02/18/1992
• Est. Priority Date: 10/15/1988
• Status: Expired due to Term

• Current Assignee: WOKA Schweisstechnik GmbH
• Original Assignee: WOKA Schweisstechnik GmbH
• Inventors: Muller, Fritz, Becker, Wilfried, Frank, Klaus, Findeisen, Eberhard
• Primary Examiner(s): THEISEN, MARY LYNN F
• Application Number:
  US07/421,670
• Time in Patent Office: 855 Days
• Field of Search: 264/8, 425/8, 75/334, 423/53, 423/440
• US Class Current: 264/8
• CPC Class Codes: C01B 32/949 Tungsten or molybdenum carbides

Abstract

To develop a process for manufacturing cast tungsten carbide spheres, without any content of spattering material, as solid spheres with a bulk weight of 0.5-11.5 g/cm³ for cast tungsten carbide spheres from a screen fraction, and with a granular distribution of 40 μm to 2,000 μm, tungsten carbide is heated to about 150°-300° C. above the melting point, and then the cast tungsten carbide is smelted and granulated in stationary inert gas.

Claims

1. Process for manufacturing cast tungsten carbide spheres with a granular distribution of 40 μ

m to 2,000 μ

m, in which cast tungsten carbide is melted from tungsten powder and carbon in a carbon-free crucible under inert gas by an arc, with the molten cast tungsten carbide being granulated under inert gas using a rotating cooled surface, wherein the cast tungsten carbide is heated to about 150°

-300°

C. above the melting point, with the cast tungsten carbide being melted and granulated under stationary inert gas.

2. Process according to claim 1, wherein a turntable with a concave shaped surface is used as the rotating cooled surface.

3. Process according to claim 1, wherein carbon black is used as the carbon.

4. Process according to claim 3, wherein the carbon black used consists of acetylene black which is obtained from the pyrolysis of ethyne.

5. Process according to claim 1, wherein rare gas is used as the inert gas.

6. Process according to claim 1, wherein an underpressure of 0.5-0.9 bar is used.

7. Process according to claim 1, wherein an underpressure of 0.8-0.85 bar is used.

8. Process according to claim 1, wherein a water-cooled cone is used as the rotating cooled surface.

9. Process according to claim 1, wherein the speed of rotation of the rotating, cooled surface is 50-600 rpm.

10. Process according to claim 1, wherein a water-cooled revolving pipe is used to provide the rotating cooled surface, and the molten cast tungsten carbide falls freely as a jet into the revolving pipe.

11. Process according to claim 10, wherein the speed of rotation of the water-cooled revolving pipe is 10-60 rpm.

12. Process according to claim 1, wherein removal of the molten cast tungsten carbide spheres following solidification takes place continuously from the granulting zone.

13. Process for manufacturing cast tungsten carbide spheres with a granular distribution of 40 μ

m to 2,000 μ

m, comprising;

melting tungsten carbide obtained from tungsten powder and carbon in a carbon-free crucible under inert gas by an arc,

heating the cast tungsten carbide to 150°

-300°

C. above the melting point and casting the molten tungsten carbide onto a rotating cooled surface to granulate it, wherein the tungsten carbide is melted and granulated under stationary inert gas.