Conductive plastic composite and its preparation and use

• US 5,158,707 A
• Filed: 09/27/1990
• Issued: 10/27/1992
• Est. Priority Date: 10/05/1989
• Status: Expired due to Fees

• Current Assignee: Neste Oy (Neste Corporation)
• Original Assignee: Neste Oy (Neste Corporation)
• Inventors: Vestberg, Torvald, Lehtiniemi, Ismo, Laakso, Jukka, sterholm, Jan-Erik
• Primary Examiner(s): Bell, Mark L.
• Assistant Examiner(s): JONES, DEBORAH D
• Application Number:
  US07/588,698
• Time in Patent Office: 761 Days
• Field of Search: 252/500, 252/518, 252/519, 526/256
• US Class Current: 252/500
• CPC Class Codes: C08G 61/126 with a five-membered ring containing one sulfur atom in the ring
• CPC Class Codes: H01B 1/127 comprising five-membered aromatic rings in the main chain, e.g. polypyrroles, polythiophenes
• CPC Class Codes: H05K 9/0079 Electrostatic discharge protection, e.g. ESD treated surface for rapid dissipation of charges
• CPC Class Codes: H05K 9/0081 Electromagnetic shielding materials, e.g. EMI, RFI shielding H05K9/0003 takes precedence

Abstract

The invention relates to the homogenization of mixtures of internally conductive polymers like 3-substituted polythiophene and matrix polymers. With an efficient homogenization the conductivity is improved when the portion of the conductive polymer is low. An efficient homogenization is achieved in the invention by mixing the internally conductive polymer with a monomer or by dissolving it into it, after which the monomer is polymerized. The plastic composites so obtained are used for several purposes in which conductivity is needed, such as EMI and ESD shielding.

Claims

1. A conductive plastic composition made by the process comprising:

a) dissolving from 0.1 to 50 percent by weight of a conductive poly(3-substituted thiophene) polymer in to a matrix monomer in liquid state, said matrix monomer being styrene;

b) polymerizing said matrix monomer into a matrix polymer by a polymerization process selected from the group consisting of suspension, emulsion and mass polymerization.

2. The composition of claim 1 wherein said matrix monomer is polymerized with a comonomer(s) selected from the group consisting of:

acrylonitrile, methacrylonitrile, 1,2-butadiene, vinyl esters, acrylic esters, methacrylic esters, maleic anhydride, alpha-methyl styrene, divinylbenzene, acrylamide, methacrylamide, and vinyl halides.

3. The conductive plastic composition of claim 1, which has been brought into conductive form by doping the conductive polymer with iodine or ferric chloride.

4. The conductive plastic composition of claim 1 wherein the poly(3-substituted thiophene) is a poly(3-alkyl thiophene).

5. A conductive plastic composite of claim 1, characterized in that its conductivity is within the range of 10^-10 -100S/cm.

6. A conductive plastic composition of claims 1, 2, 3 or 4, characterized in that it has been further melt processed by using extrusion molding, injection molding, compression molding or blown extrusion.

7. A conductive plastic composite of claims 1, 2, 3 or 4, characterized in that the internally conductive polymer contained therein also acts as a dyestuff.

8. A conductive plastic composition made by the process comprising:

a) dissolving from 0.1 to 50 percent by weight of a conductive poly(3-substituted thiophene) polymer in to a matrix monomer in liquid state, said monomer being vinyl chloride;

b) polymerizing said matrix monomer in to a matrix polymer by a polymerization process selected from the group consisting of suspension or emulsion polymerization.

9. The composition of claim 8 wherein said matrix monomer is polymerized with a comonomer(s) selected from a group consisting of:

vinyl esters, alpha-olefins, vinylidene chloride, acrylic and methacrylic esters, acrylonitriles, maleic acid esters and fumaric acid esters.

10. The conductive plastic composition of claim 8, which has been brought into conductive form by doping the conductive polymer with iodine or ferric chloride.

11. The conductive plastic composition of claim 8 wherein the poly(3-substituted thiophene) is a poly(3-alkyl thiophene).

12. A conductive plastic composite of claim 8, characterized in that its conductivity is within the range of 10^-10 -100S/cm.

13. A conductive plastic composition of claims 8, 9, 10 and 11, characterized in that it has been further melt processed by using extrusion molding, injection molding, compression molding or blown extrusion.

14. A conductive plastic composite of claims 8, 9, 10 and 11, characterized in that the internally conductive polymer contained therein also acts as a dyestuff.

15. A conductive plastic composition made by the process comprising:

a) dissolving from 0.1 to 50 percent by weight of a conductive poly(3-substituted thiophene) polymer in to a matrix monomer in liquid state, said matrix monomer being a alpha-olefin;

b) polymerizing said matrix monomer in to a matrix polymer by a polymerization process selected from the group consisting of solution and suspension.

16. The composition of claim 15 wherein said matrix monomer is polymerized with a comonomer selected from the group consisting of vinyl acetate, acrylic and methacrylic acids and esters acryl amide and acrylonitrile.

17. The conductive plastic composition of claim 15, which has been brought into conductive form by doping the conductive polymer with iodine or ferric chloride.

18. The conductive plastic composition of claim 15 wherein the poly(3-substituted thiophene) is a poly(3-alkyl thiophene).

19. A conductive plastic composite of claim 15, characterized in that its conductivity is within the range of 10^-10 -100S/cm.

20. A conductive plastic composition of claims 15, 16, 17 and 18, characterized in that it has been further melt processed by using extrusion molding injection molding, compression molding or blown extrusion.

21. A conductive plastic composite of claims 15, 16, 17 or 18, characterized in that the internally conductive polymer contained therein also acts as a dyestuff.

23. The conductive plastic composition of claim 21, which has been brought into conductive form by doping the conductive polymer with iodine or ferric chloride.

24. The conductive plastic composition of claim 21 wherein the poly(3-substituted thiophene) is a poly(3-alkyl thiophene).

25. A conductive plastic composite of claim 21, characterized in that its conductivity is within the range of 10^-10 -100S/cm.

26. A conductive plastic composition of claims 21, 22, 23 or 24, characterized in that it has been further melt processed by using extrusion molding, injection molding, compression molding or blown extrusion.

27. A conductive plastic composite of claims 21, 22, 23 or 24, characterized in that the internally conductive polymer contained therein also acts as a dyestuff.

22. A conductive plastic composition made by the process comprising:

a) dissolving from 0.1 to 50 percent by weight of a conductive poly(3-substituted thiophene) polymer into a matrix monomer in liquid state;

said matrix monomer selected from monomers that form polymers selected from the group consisting of;

polyester, polyamide, polyurethane and polysiloxane;

b) polymerizing said matrix monomer into a matrix polymer by a polymerization process selected from the group consisting of step polymerization in solution or bulk.