Glass substrate provided with a low emissivity film

• US 5,342,676 A
• Filed: 11/24/1992
• Issued: 08/30/1994
• Est. Priority Date: 11/26/1991
• Status: Expired due to Fees

• Current Assignee: Saint-Gobain Vitrage International
• Original Assignee: Saint-Gobain Vitrage International
• Inventors: Zagdoun, Georges
• Primary Examiner(s): Turner, A. A.
• Application Number:
  US07/981,083
• Time in Patent Office: 644 Days
• Field of Search: 428/216, 428/212, 428/697, 428/698, 428/428, 428/432, 428/701, 428/702, 428/704
• US Class Current: 428/216
• CPC Class Codes: C03C 17/3417 all coatings being oxide coatings
• CPC Class Codes: C03C 17/3435 comprising a nitride, oxynitride, boronitride or carbonitride
• CPC Class Codes: C03C 17/3441 comprising carbon, a carbide or oxycarbide
• CPC Class Codes: Y10T 428/24942 including components having same physical characteristic in differing degree
• CPC Class Codes: Y10T 428/24975 No layer or component greater than 5 mils thick

Abstract

The invention has as its subject a glass substrate provided with a conducting, low-emissivity transparent functional film, based upon metal oxide or oxides, on which is deposited an "outer" coating, the optical thickness of which is approximately one-quarter of the mean wavelength of the visible range, and preferably centered on 550 nm. In addition, an intermediate coating is provided between functional film and substrate, said coating having an optical thickness of from 50 to 100 nm, and preferably from 50 to 75 nm.

Claims

1. A product, comprising:

a glass substrate;

a conducting, low-emissivity transparent functional film on a first face of said glass substrate, having a refractive index of about 2 and a physical thickness of 200 to 400 nm, said functional film consisting of at least one doped metal oxide selected from the group consisting of indium oxide doped with tin, zinc oxide doped with indium, zinc oxide doped with fluorine, zinc oxide doped with aluminum, zinc oxide doped with tin, and tin oxide doped with fluorine;

an outer coating on said functional film having a refractive index less than that of the functional film, the optical thickness of the outer coating being about one-quarter of the mean wavelength centered on 550 nm; and

an intermediate coating disposed between the functional film and the glass substrate which has a refractive index less than that of the functional film and an optical thickness of between 50 and 100 nm.

2. The product according to claim 1, wherein the outer coating has a thickness of from 80 to 110 nm.

3. The product according to claim 1, wherein the intermediate coating has a physical thickness of from 30 to 50 nm.

4. The product according to any one of claims 1, 2 or 3, wherein the intermediate coating comprises at least one of the metal oxides selected from the group consisting of titanium oxide, aluminum oxide, zinc oxide, tin oxide and indium oxide.

5. The product according to any one of claims 1, 2 or 3, wherein the intermediate coating is at least one of silicon oxycarbide and silicon oxynitride.

6. The product according to any one of claims 1, 2 or 3, wherein the outer coating is based upon silicon dioxide.

7. The product according to claim 1 having a light reflection R_L of at most about 6% and a purity of colouration in reflection of at most about 3% in perpendicular incidence and an emissivity of at most about 0.2 when measured from the film side.

8. The product according to claim 1, wherein a second glass substrate is associated with the first glass substrate to form a double glazing, said double glazing having a solar factor of at least about 0.76, a colour purity in reflection of at most about 5% at variable angle of incidence.

9. The product according to claim 1, wherein the intermediate coating has an optical thickness of between 50 and 75 nm.

10. The product according to claim 1, wherein the functional film has a thickness of about 360 nm.

11. The product according to claim 1, wherein the outer coating has a refractive index of from 1.40 to 1.65.

12. The product according to claim 2, wherein the outer coating has a thickness of from 90 to 100 nm.

13. The product according to claim 1, wherein the intermediate coating has a refractive index of from 1.75 to 1.90.

14. The product according to claim 3, wherein the intermediate coating has a physical thickness of from 35 to 45 nm.