Aluminum alloy support for planographic printing plate and method for producing the same
First Claim
1. An aluminum alloy support for a planographic printing plate, which is an aluminum alloy plate comprising 0<
- Fe≦
0.20 wt %, 0≦
Si≦
0.13 wt %, Al≧
99.7 wt % and the balance of inevitable impurity elements, wherein the number of intermetallic compounds present in the arbitrary thickness direction within 10 μ
m from the plate surface is from 100 to 3,000 per mm2 and the intermetallic compound has an average particle size of from 0.5 to 8 μ
m, with the intermetallic compounds having a particle size of 10 μ
m or more being in a proportion by number of 2% or less.
2 Assignments
0 Petitions
Accused Products
Abstract
An aluminum alloy support for a planographic printing plate is disclosed, which is an aluminum alloy plate comprising 0<Fe≦0.20 wt %, 0≦Si≦0.13 wt %, Al≧99.7 wt % and the balance of inevitable impurity elements, wherein the number of intermetallic compounds present in the arbitrary thickness direction with in 10 μm from the plate surface is from 100 to 3,000 per mm2 and the intermetallic compound has an average particle size of from 0.5 to 8 μm, with the intermetallic compounds having a particle size of 10 μm or more being in a proportion by number of 2% or less. Also disclosed is a method for producing the above-described aluminum alloy support.
9 Citations
4 Claims
-
1. An aluminum alloy support for a planographic printing plate, which is an aluminum alloy plate comprising 0<
- Fe≦
0.20 wt %, 0≦
Si≦
0.13 wt %, Al≧
99.7 wt % and the balance of inevitable impurity elements, wherein the number of intermetallic compounds present in the arbitrary thickness direction within 10 μ
m from the plate surface is from 100 to 3,000 per mm2 and the intermetallic compound has an average particle size of from 0.5 to 8 μ
m, with the intermetallic compounds having a particle size of 10 μ
m or more being in a proportion by number of 2% or less. - View Dependent Claims (2)
- Fe≦
-
3. An aluminum alloy support for a planographic printing plate, which is an aluminum alloy plate comprising 0<
- Fe≦
0.20 wt %, 0≦
Si≦
0.13 wt %, Al≧
99.7 wt % and the balance of inevitable impurity elements, wherein the intermetallic compounds contained in said aluminum alloy plate and having a particle size of 0.1 μ
m or less are present at a proportion of 0.5 wt % or more of all intermetallic compounds. - View Dependent Claims (4)
- Fe≦
Specification