Method for forming silver tracks on glass

• US 5,782,945 A
• Filed: 08/21/1996
• Issued: 07/21/1998
• Est. Priority Date: 09/05/1995
• Status: Expired due to Fees

• Current Assignee: Cookson Matthey Ceramics Plc (Johnson Matthey PLC)
• Original Assignee: Cookson Matthey Ceramics Plc (Johnson Matthey PLC)
• Inventors: Rehorek, Detlef, Harris, Patricia M., Gavin, David L.
• Primary Examiner(s): Chin, Peter
• Assistant Examiner(s): Ruller, Jacqueline A.
• Application Number:
  US08/701,216
• Time in Patent Office: 699 Days
• Field of Search: 65/60.1, 65/60.2, 65/60.4, 427/125, 427/126.2, 427/126.5, 501/14, 501/17, 501/19
• US Class Current: 65/60.1
• CPC Class Codes: C03C 17/008 comprising a mixture of materials covered by two or more of the groups C03C17/02, C03C17/06, C03C17/22 and C03C17/28
• CPC Class Codes: C03C 17/06 with metals C03C17/34, C03C17/44 take precedence
• CPC Class Codes: C03C 2217/256 Ag
• CPC Class Codes: C03C 2218/119 by printing
• CPC Class Codes: C03C 8/18 containing free metals
• CPC Class Codes: H01B 1/16 the conductive material comprising metals or alloys

Abstract

A method of forming electrically conducting silver tracks on glass, by applying a silver composition comprising solids portion in a carrier medium to the glass and then firing the composition to form the tracks, wherein the solids portion contains elemental silver and/or precursor thereof and contains also elemental boron.

Claims

1. A method of forming electrically conducting silver tracks on glass, by applying a silver composition comprising solids portion in a carrier medium to the glass and then firing the composition to form the tracks, wherein the silver composition is applied onto an enamel composition on the glass, and before or after application of the silver composition, the enamel composition is fired, whereby after firing the enamel composition and the silver composition, the enamel composition obscures the silver tracks underneath from viewing through the glass;

said solids portion comprising 0.01-15 wt % elemental boron, 0-85 wt % glass frit, and the balance comprising elemental silver and/or precursors thereof.

2. A method according to claim 1 wherein the solids portion contains 10-99.5 wt % of the elemental silver and/or precursor thereof, measured as silver.

3. A method according to claim 1 wherein the elemental silver and/or precursor thereof is elemental silver.

4. A method according to claim 1 wherein the solids portion contains 0.5-7 wt % of alumina.

5. A method according to claim 1 wherein the solids portion further contains 0.5-10 wt % of metal other than silver.

6. A method according to claim 5 wherein the metal is one or more of Cu, Fe, Mn, Sn and Cr, mixtures thereof and alloys thereof.

7. A method according to claim 1 wherein the solids portion contains 0-8 wt % of glass frit and, based on the weight of the elemental silver and/or precursor thereof, measured as silver, between 0.7 and 2% of the elemental boron.

8. A method according to claim 1 wherein the silver composition and the enamel composition are fired in the same firing.

9. A method according to claim 1 wherein the enamel composition comprises glass frit, pigment and elemental boron.

10. A method according to claim 9 wherein the enamel composition contains 0.1-0.5 wt % of the boron, based on the total weight of the frit, pigment and boron.

11. A method according to claim 1 wherein the grass is bent in the firing of the silver composition.

12. A method according to claim 1 wherein the silver composition is fired at 540°

-800°

C.

13. A method according to claim 1 wherein the silver composition is fired for 2-20 minutes.

14. A method according to claim 1 wherein the glass is that for a window of a vehicle.