Anionic polymerization initiators for preparing macro-branched diene rubbers

• US 6,136,914 A
• Filed: 03/13/1998
• Issued: 10/24/2000
• Est. Priority Date: 03/13/1998
• Status: Expired due to Term

• Current Assignee: Bridgestone Corporation
• Original Assignee: Bridgestone Corporation
• Inventors: Hergenrother, William L., Cole, William M., Bohm, Georg G. A., Knutson, Theodore J.
• Primary Examiner(s): Warzel, Mark L.
• Application Number:
  US09/042,096
• Time in Patent Office: 956 Days
• Field of Search: 525/250, 525/271, 525/326.1, 525/366, 152/151, 524/495, 524/571, 524/536, 524/575
• US Class Current: 524/495
• CPC Class Codes: B60C 1/00 Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
• CPC Class Codes: C08F 36/04 conjugated
• CPC Class Codes: C08F 4/027 Polymers
• CPC Class Codes: C08F 4/46 selected from alkali metals
• CPC Class Codes: Y02T 10/86 Optimisation of rolling resistance, e.g. weight reduction
• CPC Class Codes: Y10T 152/10 Tires, resilient

Abstract

Novel solid supported anionic polymerization initiators that are multiply metalated with Group IA alkali metal atoms are provided and employed to produce extremely high molecular weight branched diene polymers. The initiators are prepared by metalating a particle comprising a thermoplastic polymer or a cured elastomer in the presence of a polar coordinator. The polymers obtained by anionic polymerization employing the initiators are multiply branched, with a polymer chain covalently attached to the particle at virtually every metalation site. The macro-branched polymers exhibit desirable properties, such as an extremely high molecular weight, a controlled molecular weight distribution, T_g and vinyl content, and the ability to readily absorb hydrocarbon solvents and oils. The polymers are easily compounded to form vulcanizable elastomeric compounds and articles that have excellent resistance to wear and tear and exhibit reduced hysteresis properties.

Claims

1. A macro-branched diene polymer having the formula

View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18)

2. The polymer of claim 1, wherein the thermoplastic polymer has a T_g of 80°

C. to about 300°

C.

3. The polymer of claim 1, wherein the cured elastomer is a compounded cured elastomer that is substantially curative free.

4. The polymer of claim 1, wherein the alkali metal atoms are lithium or sodium or potassium atoms.

5. The polymer of claim 4, wherein the alkali metal atoms are lithium atoms.

6. The polymer of claim 1, wherein the alkali metal atoms are a mixture of lithium atoms and a selection from the group consisting of atoms of sodium potassium, rubidium, cesium and francium.

7. The polymer of claim 1, wherein the polymer chain further comprises monovinyl aromatic monomer units having from about 8 to about 20 carbon atoms.

8. The polymer of claim 7, wherein the monomers are selected from the group consisting of butadiene, styrene and isoprene.

9. The polymer of claim 1, wherein n is an integer representing a multiplicity of polymer chains covalently bonded to the particle.

10. The polymer of claim 1, wherein each of the n polymer chains bonded to the particle has a number average molecular weight of about 20,000 to about 500,000.

11. The polymer of claim 1, wherein the polymer has a glass transition temperature of less than -20°

C.

12. The polymer of claim 11, wherein the glass transition temperature is less than -30°

C.

13. The polymer of claim 12, wherein the glass transition temperature is less than -35°

C.

14. A vulcanizable elastomer composition formed from the polymer of claim 1 and from about 5 to about 80 parts by weight of carbon black per 100 parts by weight of the polymer.

15. A vulcanizable elastomer composition formed from the polymer of claim 11 and from about 5 to about 80 parts by weight of carbon black per 100 parts by weight of the polymer.

16. A tire having at least one component formed from the vulcanizable elastomer composition of claim 14.

17. A tire having at least one component formed from the vulcanizable elastomer composition of claim 15.

18. The polymer of claim 1, wherein the conjugated diene monomer units comprise conjugated diolefins having from about 4 to about 12 carbon atoms.

19. A method of preparing a macro-branched diene polymer having the formula

View Dependent Claims (20, 21, 22)

20. The method of claim 19, wherein the monomer is dissolved in and the initiator is suspended in an anhydrous hydrocarbon solvent.

21. The method of claim 19, further comprising the step of terminating the polymerization with a terminating agent or a functionalizing agent.

22. The method of claim 21, wherein the terminating agent or the functionalizing agent is selected from the group consisting of alcohols, substituted aldimines, substituted ketimines, Michler'"'"'s keton, 1,3-dimethyl-2-imidazolidinone, 1-alkyl substituted pyrrolidinones, 1-aryl substituted pyrrolidinones, tributyl tin chloride, and mixtures thereof.