Electrochromic devices with improved processability and methods of preparing the same

• US 6,327,069 B1
• Filed: 11/08/1999
• Issued: 12/04/2001
• Est. Priority Date: 10/26/1994
• Status: Expired due to Fees

• Current Assignee: Donnelly Corporation (Magna International Incorporated)
• Original Assignee: Donnelly Corporation (Magna International Incorporated)
• Inventors: Grimes, F. Randall, Bigelow, Barbara A., Agrawal, Anoop, Allemand, Pierre-Marc
• Primary Examiner(s): Epps, Georgia
• Assistant Examiner(s): Spector, David N.
• Application Number:
  US09/435,904
• Time in Patent Office: 757 Days
• Field of Search: 359/265, 359/270, 359/272, 359/273, 359/274, 359/275, 428/426, 428/430, 428/432, 428/441, 428/690
• US Class Current: 359/265
• CPC Class Codes: G02F 1/15165 Polymers
• CPC Class Codes: Y10T 428/31616 Next to polyester [e.g., alkyd]
• CPC Class Codes: Y10T 428/31645 Next to addition polymer from unsaturated monomers

Abstract

Electrochromic devices and processes for preparing the same are provided which do not require a separate process step of ion intercalation by employing an electrochromically-inert reducing or oxidizing additive in the electrochemically active material or the electrolyte of the electrochromic devices.

Claims

1. A process for preparing an electrochemically active layer on a substrate comprising the steps of:

(a) forming a liquid mixture of an electrochemically active material and an electrochromically-inert additive selected from the group consisting of reducing agents and oxidizing agents;

(b) contacting the liquid mixture to the substrate; and

(c) optionally exposing said contacted substrate to a temperature for a sufficient length of time for the electrochromically-inert additive to reduce or oxidize the electrochemically active material.

2. The process according to claim 1, wherein the electrochemically active material is an electrochemically active polymeric material.

3. The process according to claim 2, wherein the electrochemically active polymeric material is selected from the group consisting of polyaniline, a polyaniline derivative and mixtures thereof.

4. The process according to claim 1, wherein the substrate is a conductive coated substrate.

5. The process according to claim 4, wherein the conductive coating on said substrate is selected from the group consisting of doped indium oxide, doped tin oxide and doped zinc oxide.

6. The process according to claim 1, wherein the electrochromically-inert additive is at least one reducing agent.

7. The process according to claim 6, wherein the reducing agent is selected from the group consisting of oxalic acid, ascorbic acid, mercaptans, hydrazines, amines, organo lithium and mixtures thereof.

8. The process according to claim 1, wherein the electrochromically-inert additive is at least one oxidizing agent.

9. The process according to claim 8, wherein the oxidizing agent is selected from the group consisting of persulfates, peroxides, nitrosonium salts and mixtures thereof.

10. A process for preparing an electrochromic device having two opposed electrodes, at least one of which is transparent, an electrochemically active layer disposed on an opposing face of one of said electrodes and an electrolyte disposed between said electrochemically active layer and an other opposing face of said electrodes, said process comprising the steps of:

(a) forming said electrochemically active layer on said opposing face of one of said electrodes by contacting said opposing face with a liquid mixture of an electrochemically active material and an electrochromically-inert additive selected from the group consisting of reducing agents and oxidizing agents;

(b) optionally exposing said liquid mixture contacted opposing face to a temperature for a sufficient length of time for the electrochromically-inert additive to reduce or oxidize the electrochemically active material;

(c) assembling said electrodes in a spaced-apart opposing relationship with said electrochemically active layer facing said other opposing face of said electrodes to form a cell; and

(d) filling said cell with an electrolyte.

11. The process according to claim 10, wherein the electrochemically active material is an electrochemically active polymeric material.

12. The process according to claim 11, wherein the electrochemically active polymeric material is selected from the group consisting of polyaniline, a polyaniline derivative and mixtures thereof.

13. The process according to claim 10, wherein the conductive coating on said substrate is selected from the group consisting of doped indium oxide, doped tin oxide and doped zinc oxide.

14. The process according to claim 10, wherein the electrochromically-inert additive is at least one reducing agent.

15. The process according to claim 14, wherein the reducing agent is selected from the group consisting of oxalic acid, ascorbic acid, mercaptans, hydrazines, amines, organo lithium and mixtures thereof.

16. The process according to claim 10, wherein the electrochromically-inert additive is at least one oxidizing agent.

17. The process according to claim 16, wherein the oxidizing agent is selected from the group consisting of persulfates, peroxides, nitrosonium salts and mixtures thereof.

18. The process according to claim 10, wherein a first substrate is disposed on a non-opposing surface of one of said electrodes and a second substrate is disposed on an other non-opposing surface of said electrodes, wherein at least one of said substrates is transparent.

19. The process according to claim 18, wherein one of said substrates is reflective.

20. The process according to claim 10, wherein one of said electrodes is reflective.

21. The process according to claim 10, wherein the electrochemically active material is an inorganic material.

22. The process according to claim 10, further comprising the step of forming a second electrochemically active layer on the other opposing face of said electrodes.

23. A process for preparing an electrochromic device having two opposed electrodes, at least one of which is transparent, an electrochemically active layer disposed on an opposing face of one of said electrodes and an electrolyte disposed between said electrochemically active layer and an other opposing face of said electrodes, said process comprising the steps of:

(a) forming said electrochemically active layer comprised of an electrochemical active material on said opposing face of one of said electrodes;

(b) assembling said electrodes in a spaced-apart opposing relationship with said electrochemically active layer facing said other opposing face of said electrodes to form a cell;

(c) filling said cell with an electrolyte containing an electrochromically-inert additive selected from the group consisting of reducing agents and oxidizing agents; and

(d) optionally exposing said filled cell to a temperature for a sufficient length of time for the electrochromically-inert additive to reduce or oxidize said electrochemically active material.

24. The process according to claim 23, wherein the electrochemically active material is an electrochemically active polymeric material.

25. The process according to claim 24, wherein the electrochemically active polymeric material is selected from the group consisting of polyaniline, a polyaniline derivative and mixtures thereof.

26. The process according to claim 23, wherein the at least one transparent conductive electrode is selected from the group consisting of doped indium oxide, doped tin oxide and doped zinc oxide.

27. The process according to claim 23, wherein the electrochromically-inert additive is at least one reducing agent.

28. The process according to claim 27, wherein the reducing agent is selected from the group consisting of oxalic acid, ascorbic acid, mercaptans, hydrazines, amines, organo lithium and mixtures thereof.

29. The process according to claim 23, wherein the electrochromically-inert additive is at least one oxidizing agent.

30. The process according to claim 29, wherein the oxidizing agent is selected from the group consisting of persulfates, peroxides, nitrosonium salts and mixtures thereof.

31. The process according to claim 23, wherein a first substrate is disposed on a non-opposing surface of one of said electrodes and a second substrate is disposed on an other non-opposing surface of said electrodes.

32. The process according to claim 31, wherein one of said substrates is reflective.

33. The process according to claim 23, wherein one of said electrodes is reflective.

34. The process according to claim 23, wherein the electrochemically active material is an inorganic material.

35. The process according to claim 23, further comprising the step of forming a second electrochemically active layer on the other opposing face of said electrodes.