Composite rim

• US 6,347,839 B1
• Filed: 09/25/2000
• Issued: 02/19/2002
• Est. Priority Date: 09/25/2000
• Status: Expired due to Term

• Current Assignee: Reynolds Cycling, LLC
• Original Assignee: The Polymeric Corporation
• Inventors: Steinke, Richard A., Lew, Paul
• Primary Examiner(s): Morano, S. Joseph
• Assistant Examiner(s): NGUYEN, LONG B
• Application Number:
  US09/668,867
• Time in Patent Office: 512 Days
• Field of Search: 301/95, 301/64.7, 301/89, 301/104, 301/54, 301/55, 301/56, 301/57, 264/640, 264/641, 264/642
• US Class Current: 301/95.102
• CPC Class Codes: B29C 70/345 using matched moulds
• CPC Class Codes: B29L 2031/3091 Bicycles
• CPC Class Codes: B29L 2031/322 made wholly of plastics
• CPC Class Codes: B60B 21/04 with substantially radial flanges with rail-engaging flanges B60B17/00 B60B21/021 takes precedence
• CPC Class Codes: B60B 21/062 for bicycles
• CPC Class Codes: B60B 5/02 made of synthetic material
• CPC Class Codes: B60Y 2200/13 Bicycles; Tricycles

Abstract

A composite bicycle tire rim constructed from layers or plys of a fiber reinforcement, preferably fiber glass, to provide a rim that has a weight that is comparable to an aluminum rim and as is strong as a steel rim. The composite rim is continuous, is formed as a hooked bead type rim to have inwardly pointing side wall hook ends that are for fitting into grooves formed in a tire side walls, mounting the tire thereto. The rim is formed on a circular mandrel by laying up groups of plys thereon, with four (4) plys of fiber glass laid up for each group. In which laying up, a first ply of the four plys is fitted onto the mandrel to where its fiber angle is parallel to the mold mandrel circumference, with a following ply laid thereon at a selected positive angle to a vertical axis, and a next ply is laid thereon at a negative angle to the vertical axis, and with a final ply of each group laid thereon to have its fibers perpendicular to a tangent to the mold circumference. Which fiber placement, for each group, creates a balanced laminate, without residual stress, that is not subject to dimensional deformity. The mandrel with the groups of fiber glass plys thereon, is placed in a mold cavity, wherein the laminate is subjected to heat and pressure to cure it into the composite rim that is removed from the mold and the mandrel cross section is reduced to allow it to be removed from between the rim hook ends. Which hook ends are machined to a desired length from the rim side walls inner surfaces, and the rim is coated with a urethane polymer to enhance the overall rim strength and provide an attractive surface finish.

Claims

1. A composite rim comprising a seamless uniform continuous unit by laying up and curing plys of resin coated fibrous material where the fibers of each said ply of fibrous material are positioned at a selected crossing angle onto the fibers of the ply that it is laid upon, said rim to have upstanding side walls that extend from along parallel edges of rim side walls to receive a tire fitted therein and including inwardly pointing hook ends formed to extend toward one another from top ends of the rim side wall with each said hook end for fitting each said hook end for fitting to a tire side wall rim mounting means.

2. The bicycle rim as recited in claim 1, wherein the rim is formed by laying up successive groups of four (4) plys of a resin coated fiberglass material as a laminate onto a mandrel whose width dimension can be shortened, after curing, to allow said mandrel to pass between the rim hook ends and the fibers of a first ply of said four (4) plys of fiber glass is laid onto the mandrel at an angle of approximately zero (0) degrees to a center plane extending across and bisecting said mold and parallel to the circumference of said mold, a second ply laid over said first ply with its fibers at an angle of plus thirty eight (38) degrees, plus or minus five (5) degrees to said center plane, a third ply laid over said second ply with its fibers at an angle of minus thirty eight (38) degrees, plus or minus five (5) degrees to said center plane, and a fourth ply laid over said third ply with its fibers at an angle of approximately ninety (90) degrees to said center plane, and is perpendicular to a tangent to said mold circumference.

3. The composite rim as recited in claim 2, wherein the rims is formed from six (6) groups of four (4) plys for each group.

4. The composite rim as recited in claim 3, wherein each group of four (4) plys has a thickness of from twenty eight (28) to thirty four (34) one thousandth (1000) of an inch.

5. The composite rim as recited in claim 4, wherein the six (6) groups of plys are laid up upon the mandrel which is then fitted into a mold cavity that is closed and heat and pressure are applied to the laminate between the walls of said mandrel and mold cavity, curing the laminate into a continuous rim which after removal of said rim from the mold cavity, the mandrel is removed from within the rim and the hook ends extending from the tops of the rim side walls are machined, as required, to extend a distance out from said side wall top edges.

6. The composite rim as recited in claim 5, further including coating the composite rim exterior surface with a urethane polymer coating.

7. The composite rim as recited in claim 6, wherein the rim interior is coated with a urethane polymer coating.