Medical device including improved expandable balloon

• US 7,485,250 B2
• Filed: 06/16/2003
• Issued: 02/03/2009
• Est. Priority Date: 09/17/1999
• Status: Active Grant

• Current Assignee: Cook Medical Incorporated (Cook Group Incorporated)
• Original Assignee: Cook Incorporated (Cook Group Incorporated)
• Inventors: Burton, David G., Boatman, Scott E., Hoffa, Michael C., Drewes, David A. Jr., Lessard, David R., Hupcey, Maggie A. Z.
• Primary Examiner(s): Huson; Monica A
• Assistant Examiner(s): WOLLSCHLAGER, JEFFREY MICHAEL
• Application Number:
  US10/463,749
• Publication Number:
  US 20040073164A1
• Time in Patent Office: 2,059 Days
• Field of Search: None
• US Class Current: 264/494
• CPC Class Codes: A61L 29/06 obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: C08F 218/16 with alcohols containing three or more carbon atoms
• CPC Class Codes: C08F 283/04 on to polycarbonamides, polyesteramides or polyimides C08F283/004 takes precedence
• CPC Class Codes: C08G 69/48 Polymers modified by chemical after-treatment
• CPC Class Codes: C08L 77/00 Compositions of polyamides obtained by reactions forming a carboxylic amide link in the main chain of polyhydrazides C08L79/06; of polyamideimides or polyamide acids C08L79/08; Compositions of derivatives of such polymers

Abstract

A medical device (10) includes a catheter shaft (11) including inner and outer catheter shafts (12 and 14), and an expandable balloon (18) carried by the catheter shaft (11). The balloon (18) is made from an irradiation cross-linked mixture of a polyamide elastomer and at least one additional cross-linking reactant. The polyamide elastomer can be a polyester amide, a polyether ester amide or a polyether amide, and is preferably a nylon block copolymer. The cross-linking reactant can be: (a) a difunctional material, (b) a trifunctional material, (c) a tetrafunctional material, or (d) an aromatic molecule containing at least two ring substituents, each of the ring substituents having labile hydrogens at a benzylic site therein. The cross-linking reactant can also be diallyl phthalate or meta-phenylene dimaleimide. Irradiation is carried out by exposure to an electron beam or to ultraviolet, X- or gamma radiation, preferably at a total fluence of about 0.5 to about 20 megarads. The amount of the cross-linking reactant is selected to avoid the formation of gelling during the process by which the balloon (18) is made, and the amount of the cross-linking agent and the irradiation fluence are selected to give the balloon a strength generally about equal to that which would be obtained by mere irradiation.

Claims

1. A process for assembling a medical device, the medical device comprising an expandable balloon, and the process comprising:

creating a mixture of a polyamide elastomer and at least one additional cross-linking reactant, the cross-linking reactant comprising an aromatic molecule selected from the class consisting of 1,3,5 triethyl benzene;

1,2,4 triethyl benzene; and

1,3,5 triisopropyl benzene;

cross-linking the mixture of the polyamide elastomer and the at least one additional reactant by exposing the mixture to a suitable fluence of radiation; and

forming the cross-linked mixture into the balloon.

2. The process according to claim 1,

wherein the step of cross-linking the mixture of the polyamide elastomer and the at least one additional reactant involves cross-linking the at least one additional reactant with the polyamide elastomer.

3. The process according to claim 1, wherein the process is carried out with about 0.5 to about 1.5 percent by weight of the aromatic molecule.

4. The process according to claim 1, wherein the process is carried out with an amount of the at least one cross-linking reactant sufficient to give the balloon a strength about equal to that of a balloon composed of a nylon block copolymer and comparably cross-linked by irradiation, but in the absence of any cross-linking reactant, agent or promoter.

5. The process according to claim 1, wherein cross-linking of the mixture of the polyamide elastomer and the at least one additional reactant comprises irradiating the mixture with an electron beam or with ultraviolet, X-rays or gamma rays.

6. The process according to claim 1, wherein the cross-linking of the mixture of the polyamide elastomer and the at least one additional reactant is carried out at a total fluence of about 0.5 to about 20 megarads.

7. The process according to claim 1, wherein the mixing of the polyamide elastomer and the at least one additional reactant is carried out by compounding.

8. The process according to claim 1, further comprising forming the mixture of the polyamide elastomer and the at least one additional reactant into tubing, from which the balloon is formed.

9. The process according to claim 8, wherein the tubing is formed by extruding the mixture of the polyamide elastomer and the at least one additional reactant.

10. The process according to claim 8, wherein the mixture of the polyamide elastomer and the at least one additional reactant is formed into the balloon by inflation of the tubing.

11. The process according to claim 1, wherein the medical device further comprises a catheter shaft, and wherein the process further comprises connecting the balloon to the catheter shaft.

12. The process according to claim 11, wherein connecting the balloon to the catheter shaft is carried out by adhesion.

13. The process according to claim 11, wherein connecting the balloon to the catheter shaft is carried out by thermal bonding.

14. The process according to claim 1, wherein the process is carried out with at least one polyamide elastomer selected from the class consisting of polyester amides, polyether ester amides and polyether amides.

15. The process according to claim 14, wherein the process is carried out with a polyamide elastomer comprising a nylon block copolymer.

16. The process according to claim 15, wherein the process is carried out with a nylon block copolymer including polyether blocks separated by polyamide blocks.