Method of producing an interpenetrating polymer network (IPN), the IPN and use thereof

• US 7,687,585 B2
• Filed: 07/02/2004
• Issued: 03/30/2010
• Est. Priority Date: 07/04/2003
• Status: Active Grant

• Current Assignee: PTT Holding ApS
• Original Assignee: Biomodics ApS
• Inventors: Karthauser, Joachim
• Primary Examiner(s): PENG, KUO LIANG
• Application Number:
  US10/563,130
• Publication Number:
  US 20060148985A1
• Time in Patent Office: 2,097 Days
• Field of Search: 525/474, 525/479, 427/536
• US Class Current: 525/474
• CPC Class Codes: C08F 283/12 on to polysiloxanes
• CPC Class Codes: Y02P 20/54 using solvents, e.g. supercritical solvents or ionic liquids

Abstract

The invention comprises a method of producing an interpenetrating polymer network (IPN) comprising the steps of I) providing a silicone polymer composition; (ii) providing one or more monomers for a polymer; (iii) providing a solvent for the one or more monomers; iv) exposing said silicone polymer composition to said one or more monomers and said solvent to precipitate monomer within said silicone polymer composition and v) polymerizing said monomer to form an IPN, wherein said solvent has a surface tension at the exposing step of about 15 mNZm or less. It is preferred that the solvent, which is preferably CO₂, in the exposing step is in or near its supercritical state. The method is fast and simple, and the dispersion of the monomers may be controlled to thereby control the amount and distribution of the interpenetrating network in the silicone material. Further more the method results in new materials, where silicone polymers are used as the basic materials.

Claims

1. A method of producing an interpenetrating polymer network (IPN) comprising the steps of

i) providing a silicone polymer composition,

ii) providing one or more monomers for a polymer,

iii) providing a solvent for the one or more monomers,

iv) exposing said silicone polymer composition to said one or more monomers and said solvent to precipitate monomer within said silicone polymer composition and

v) polymerizing said monomer to form an IPN,

wherein said solvent has a surface tension at the exposing step of about 15 mN/m or less.

2. A method of producing an IPN according to claim 1, wherein said solvent has a surface tension in liquid form of about 15 mN/m or less.

3. A method of producing an IPN according to claim 1, wherein said silicone polymer composition comprises at least 10% by weight of polymer having a backbone consisting of Si and O molecules.

4. A method of producing an IPN according to claim 1, wherein said silicone polymer composition comprises at least 10% by weight of polymer having a backbone consisting of Si molecules.

5. A method of producing an IPN according to claim 1, wherein said silicone polymer composition comprises at least 10% by weight of polysiloxane polymer.

6. A method of producing an IPN according to claim 1, wherein said silicone polymer composition comprises one or more polymers selected from the group consisting of dimethyl polysiloxane, methylphenyl polysiloxane, fluorosilicone rubber, silicone esters, polysiloxanes, polysilanes, polychlorosilanes, polyalkoxysilanes, polyaminosilanes, polydialkylsiloxanes, and polysiloxanes containing phenyl substituents, said polymers of the silicone polymer composition optionally being vinyl-functionalized and/or optionally being partially or fully fluorinated.

7. A method of producing an IPN according to claim 1, wherein said silicone polymer composition comprises up to 90% by weight of non-silicone polymers or co-polymers, fillers and/or additives, said non-silicone polymers being thermoplastics or thermosets, and being selected from polyolefins, polyesters, polyurethanes, polycarbonates, and polyvinyl polymers, said fillers being particles or fibres in the form of minerals or organic fillers, and being selected from silica, metals, metal oxides, mixed metal oxides, glass beads and glass fibers, and additives being selected from adhesion promoters, process and plasticizing oils, antioxidants and pigments.

8. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is partially vulcanized.

9. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is a vulcanized rubber.

10. A method of producing an IPN according to claim 1, wherein said one or more monomers are dissolvable in said solvent when said solvent is in liquid state, in gas state or in supercritical state.

11. A method of producing an IPN according claim 1, wherein said one or more monomers comprise at least 1% by weight of one or more of the monomers selected from silicone containing monomers, olefins, styrene, vinylpyrrolidone, oxygen- and nitrogen-containing monomers, aromatic compounds, aromatic resins, imadazol and imidazol derivatives, pyrazoles, quaternary ammonium compounds, polyurethane prepolymers and epoxy resins.

12. A method of producing an IPN according to claim 1, wherein said one or more monomers comprise at least 50% by weight of vinylpyrrolidone.

13. A method of producing an IPN according to claim 1, wherein said one or more monomers comprise at least 50% by weight of olefins.

14. A method of producing an IPN according to claim 1, wherein said one or more monomers comprise at least 50% by weight of silanes.

15. A method of producing an IPN according to claim 1, wherein said one or more monomers are free radical polymerizable.

16. A method of producing an IPN according to claim 1, wherein the solvent is one or more hydrocarbons or carbon-containing compounds or a composition comprising hydrocarbons or carbon-containing compounds with a Hildebrand solubility of below 11, the silicone polymer composition being exposed to the solvent in its supercritical state or near its supercritical state, where the term ‘

near its supercritical state’

means that the total pressure is at least 10 bar.

17. A method of producing an IPN according to claim 1, wherein the solvent comprises one or more compounds from the group of C₁-C₁₂ hydrocarbons or carbon-containing compounds, methanol, acetone, N₂O and CO₂, the silicone polymer composition being exposed to the solvent in supercritical state.

18. A method of producing an IPN according to claim 1, wherein the solvent has a surface tension in liquid form of about 15 mN/m or less, the silicone polymer composition being exposed to the solvent while it is in one or more of its states liquid state, gas state and supercritical state.

19. A method of producing an IPN according to claim 18, wherein said solvent comprises at least 50% by weight of one or more of the components selected from the group consisting of CO₂, and N₂O and C₁-C₅ hydrocarbons, the solvent comprising at least 50% by weight of CO₂.

20. A method of producing an IPN according to claim 1, wherein the solvent comprises a surfactant selected from anionic, cationic, non-ionic and amphoteric surfactants, said solvent comprising up to 5% by weight of surfactant.

21. A method of producing an IPN according to claim 1, wherein a radical starter is incorporated into said silicone polymer, by physical compounding, by swelling or impregnation in dissolved condition, or by co-impregnation with the one or more monomers, the amount of radical starter being sufficient to initiate the polymerization.

22. A method of producing an IPN according to claim 21, wherein the amount of radical starter is at least 0.01 mol % of the monomer.

23. A method of producing an IPN according to claim 21, wherein said radical starter is selected from peroxides, azo-compounds, and photo-labile compounds, said radical starter being heat- or radiation activatable.

24. A method of producing an IPN according to claim 1, wherein said one or more monomers are dissolved in the solvent together with a radical starter, the amount of radical starter being sufficient to initiate the polymerization.

25. A method of producing an IPN according to claim 1, wherein said monomer is dissolved in liquid solvent, said silicone polymer composition being exposed to said solvent while the solvent is in liquid state, in gas state and/or supercritical state.

26. A method of producing an IPN according to claim 1, wherein said monomer is dissolved in gas solvent, said silicone polymer composition being exposed to said solvent while the solvent is in liquid state, in gas state and/or in supercritical state.

27. A method of producing an IPN according to claim 1, wherein said monomer is dissolved in supercritical solvent, said silicone polymer composition being exposed to said solvent while the solvent is in liquid state, in gas state and/or in supercritical state.

28. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is exposed to said solvent for a sufficient time to swell the silicone polymer composition with at least 0.01% by weight of solvent calculated on the weight of the silicone polymer composition.

29. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is exposed to said solvent under varying pressure, the pressure being decreased after at least part of the solvent has been swelled into the silicone polymer composition whereby monomer(s) precipitate within the silicone composition.

30. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is exposed to said solvent under varying temperature, the temperature being decreased after at least part of the solvent has been swelled into the silicone polymer composition whereby monomer(s) precipitate within the silicone composition.

31. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is exposed to said solvent under conditions where the solvent is in a first state, followed by a change of conditions whereby the solvent changes to a second state, said first state being liquid state or supercritical state and said second state being gas state.

32. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is exposed to said solvent with said one or more monomers for a sufficient time to precipitate at least 0.01% by weight of monomer(s) of the total weight of the silicone polymer composition.

33. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is exposed in two or more steps to said solvent with one or more monomers to provide at total monomer precipitation of at least 0.01% by weight of monomer(s) of the total weight of the silicone polymer composition, said two or more steps being equal or different from each other with respect to solvent, monomer amounts and/or exposing time.

34. A method of producing an IPN according to claim 31, wherein said silicone polymer composition is exposed to said solvent with said one or more monomers for a total time of at least 1 min.

35. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is treated with the solvent in or near its supercritical state followed by feeding of the monomer into the reaction chamber where the monomer is dissolved in the solvent in or near its supercritical state while the silicone polymer composition simultaneously is exposed to the solvent.

36. A method of producing an IPN according to claim 1, wherein said silicone polymer composition is exposed to a solvent consisting essentially of carbon dioxide and carrying the monomer(s) in or near its supercritical state, for a sufficient time to swell the silicone polymer composition with the solvent carrying the monomer(s).

37. A method of producing an IPN according to claim 1, wherein said silicone polymer composition prior to the exposing step is shaped, by extrusion, injecting-moulding, calendering, pressing or cutting.

38. A method of producing a polymeric unit comprising:

producing an IPN unit in a desired shape by a method according to claim 1, and

treating the surface thereof by plasma or flame surface activation and subsequent painting, or immediate painting or coating.

39. A method of producing a polymeric unit according to claim 38 wherein the silicon polymer composition used for the IPN is transparent.

40. A method of producing a polymer unit according to claim 38, wherein the one or more monomers comprise one or more monomers selected from styrene, acrylics and urethanes.

41. An automotive part comprising a polymeric unit obtained by a method according to claim 38.

42. A telecom part comprising a polymeric unit obtained by a method according to claim 38.

43. A medical device selected from catheter, part of a pace maker and an implant, comprising a polymeric unit obtained by a method according to claim 38.

44. A method of producing a polymer membrane comprising:

producing an IPN unit shaped as a membrane by a method according to claim 1, wherein the membrane has a thickness between 5 and 1000 μ

m.

45. A method of producing a polymer membrane according to claim 44, wherein the amount of monomer precipitated into the silicone polymer composition is 5% by weight or less.

46. A method of producing a polymer membrane according to claim 44, wherein the membrane is a membrane for separation of gases or liquids.

47. A method of producing a polymer membrane according to claim 44, wherein the membrane is a fuel cell membrane, said membrane being less permeable to gases than the original silicone composition at least by a factor of 2, and whereby the conductivity for protons (H⁺) is increased in comparison with the original silicone composition by incorporation of proton-conducting monomers, the conductivity for protons (H⁺) being increased in comparison with the original silicone composition by a factor or at least 10.