Soft prosthesis shell texturing method

• US 8,313,527 B2
• Filed: 10/30/2008
• Issued: 11/20/2012
• Est. Priority Date: 11/05/2007
• Status: Active Grant

• Current Assignee: Allergan, Inc. (Canada) (Abbvie Incorporated)
• Original Assignee: Allergan, Inc. (Canada) (Abbvie Incorporated)
• Inventors: Powell, Thomas E., Dang, Loantrang
• Primary Examiner(s): Isabella, David
• Assistant Examiner(s): IWAMAYE, ANDREW MICHAEL
• Application Number:
  US12/261,939
• Publication Number:
  US 20090118829A1
• Time in Patent Office: 1,482 Days
• Field of Search: 623/8, 623 2372- 2376, 427/2.24
• US Class Current: 623/8
• CPC Class Codes: A61F 2/0077 Special surfaces of prostheses, e.g. for improving ingrowth A61F2/30767 takes precedence
• CPC Class Codes: A61F 2/12 Mammary prostheses and implants
• CPC Class Codes: A61F 2002/0086 for preferentially controlling or promoting the growth of specific types of cells or tissues of bone tissue onto implantable joints A61F2002/3093

Abstract

A method of texturing a soft prosthetic implant shell, such as a silicone breast implant shell. A soft prosthetic implant with a textured external surface layer of silicone elastomer and having an open-cell structure is made by adhering and then dissolving round salt crystals. The resulting roughened surface has enhanced physical properties relative to surfaces formed with angular salt crystals. An implant having such a textured external surface layer is expected to help prevent capsular contraction, to help prevent scar formation, and to help in anchoring the implant within the body.

Claims

1. A soft prosthetic breast implant, formed by a process comprising:

forming a flexible shell of silicone elastomer, the silicone elastomer having a thickness;

adhering on the exterior of the flexible shell an even distribution of round particles;

curing the flexible shell with the round particles adhered thereto; and

removing the round particles thereby forming an open-pored structure on the exterior of the flexible shell such that the exterior of the flexible shell exhibits an undulating topography, the open pored-structure comprising round open cavities defined by impressions of the round particles;

processing the flexible shell such that it forms a closed envelope;

wherein the flexible shell formed by the process has at least one of the physical properties of ultimate break force, ultimate elongation, or ultimate tensile strength that is superior to such physical property of an identical flexible shell made using the same process and same materials except for angular particles instead of round particles;

wherein the round particles have a substantially uniform particle size within a particle size range selected from a group of ranges consisting of (1) a range between 180 microns and 425 microns, (2) a range between 425 microns and 850 microns, and (3) a range between 850 microns and 1450 microns; and

wherein the open-pored structure does not extend through the entire thickness of the silicone elastomer.

2. The breast implant of claim 1, wherein the particles are round salt particles.

3. The breast implant of claim 1, wherein the step of forming the flexible shell comprises dipping a mandrel into a liquid dispersion of an elastomeric material.

4. The breast implant of claim 3, wherein the step of forming the flexible shell comprises rotationally molding the shell.

5. The breast implant of claim 3, wherein the round particles are sodium chloride crystals.

6. The breast implant of claim 1 wherein the ultimate break force of the flexible shell is more than 5% greater than the ultimate break force of said identical flexible shell made using the same process and same materials except for angular particles instead of round particles.

7. The breast implant of claim 1 wherein the ultimate elongation of the flexible shell is more than 6% greater than the ultimate elongation of said identical flexible shell made using the same process and same materials except for angular particles instead of round particles.

8. The breast implant of claim 1 wherein the ultimate tensile strength of the flexible shell is 3% greater than an ultimate tensile strength of said identical flexible shell made using the same process and same materials except for angular particles instead of rounded round particles.

9. The breast implant of claim 1 wherein about 90% of the round particles are in the selected particle size range.

10. The breast implant of claim 1 wherein the selected particle size range is the range between 850 microns and 1450 microns.

11. The breast implant of claim 1 wherein the selected particle size range is the range between 425 microns and 850 microns.

12. The breast implant of claim 1 wherein the selected particle size range is the range between 180 microns and 425 microns.