Low solar absorbing blue glass, solar reflecting coated blue glass, and insulating unit having a low solar heat gain

• US 8,455,066 B2
• Filed: 08/20/2012
• Issued: 06/04/2013
• Est. Priority Date: 03/28/2006
• Status: Active Grant

• Current Assignee: Vitro Flat Glass LLC (Compagnie De Saint-Gobain)
• Original Assignee: PPG Industries Ohio Incorporated (Nouryon BV)
• Inventors: Heithoff, Robert B., Miner, Glenn T.
• Primary Examiner(s): SAMPLE, DAVID R
• Application Number:
  US13/589,353
• Publication Number:
  US 20120315410A1
• Time in Patent Office: 288 Days
• Field of Search: None
• US Class Current: 428/34
• CPC Class Codes: C03C 17/3411 with at least two coatings of inorganic materials C03C17/36, C03C17/42 take precedence
• CPC Class Codes: C03C 17/36 at least one coating being a metal
• CPC Class Codes: C03C 17/366 Low-emissivity or solar control coatings
• CPC Class Codes: C03C 17/3681 the multilayer coating being used in glazing, e.g. windows or windscreens
• CPC Class Codes: C03C 3/087 containing calcium oxide, e.g. common sheet or container glass
• CPC Class Codes: C03C 3/095 containing rare earths
• CPC Class Codes: C03C 4/02 for coloured glass
• CPC Class Codes: C03C 4/082 for infrared absorbing glass
• CPC Class Codes: C03C 4/085 for ultraviolet absorbing glass
• CPC Class Codes: E06B 9/24 Screens or other constructions affording protection against light, especially against sunshine; Similar screens for privacy or appearance; Slat blindsoperating, guiding or securing devices or arrangements for roll-type closures E06B9/56; free-hanging flexible screens A47H23/00

Abstract

An insulating unit having a neutral grey color and a solar heat gain coefficient less than 0.40 includes a clear glass sheet spaced from a coated glass sheet. The coated glass sheet includes a colored glass substrate having a solar infrared reflective coating. The composition of the coated substrate includes a base glass portion and a glass colorant portion, the glass colorant portion including total iron in the range of 0.04 to less than 0.28 weight percent; CoO in the range of 32 to 90 parts per million, and Se in the range of greater than 0 to less than 5.5 parts per million. In one non-limiting embodiment of the invention the glass substrate at a thickness of 0.223 inches has a* chromaticity coordinates of −3.5 to +2.5 and b* chromaticity coordinates of −1 to −15, and a visible light transmittance of 40 to 80%.

Claims

1. A coated glass article comprising, a glass substrate and a coating over a major surface of the glass substrate, the glass substrate comprising a base glass portion and a glass colorant portion, the glass colorant portion having colorants in selected amounts to provide the glass substrate with chromaticity coordinates of a* in the range of −

3.5 to +2.5 and b* in the range of −

1 to −

15, and a visible light transmittance of 40 to 80% at a reference thickness of 0.223 inches (5.66 mm), and the coated glass article has a hemispherical emissivity of no greater than 0.25.

2. The coated glass article according to claim 1, wherein the coated article, has chromaticity coordinates of a* in the range of −

7.0 to +2 and b* in the range of 3 to −

13, and a visible light transmittance of in the range of 26 to 75% at a reference thickness of 0.223 inches (5.66 mm).

3. The coated glass article according to claim 2, wherein the glass substrate has chromaticity coordinates of a* in the range of −

3 to +1 and b* in the range of −

2 to −

10 at a reference thickness of 0.223 inches (5.66 mm), and the coated glass article has chromaticity coordinates of a* in the range of −

6 to +0.5 and b* in the range of 2 to −

9, a visible light transmittance of in the range of 36 to 71% at a reference thickness of 0.223 inches (5.66 mm), and a hemispherical emissivity of no greater than 0.10.

4. The coated glass article according to claim 2, wherein the glass substrate comprises a base glass portion and a glass colorant portion, the glass colorant portion comprising:

total iron in the range of 0.08 to 0.26 weight percent;

CoO in the range of 35 to 60 parts per million,

Se in the range of 1 to 5 parts per million, and

a ratio CoO to Se, each expressed in parts per million, of least 7.

5. The coated glass article according to claim 4, wherein the coating is an infrared reflective coating comprising a silver film between a pair of dielectric films, and the coated glass article has a* chromaticity coordinates in the range of −

3 to 0.5 and b* chromaticity coordinates in the range of 0 to −

8, and a visible light transmittance of 45 to 71% at a reference thickness of 0.223 inches (5.66 mm).

6. The coated glass article according to claim 5, wherein the glass substrate has a* chromaticity coordinates in the range of −

3 to +1 and b* chromaticity coordinates in the range of −

2 to −

10 at a reference thickness of 0.223 inches (5.66 mm).

7. The coated glass article according to claim 4, wherein the coated glass article has a hemispherical emissivity of no greater than 0.10.

8. The coated glass article according to claim 7, wherein the coating is an infrared reflective coating comprising a first silver film over a first dielectric film, a second dielectric film over the first silver film, a second silver layer over the second dielectric film, and a third dielectric film over the second silver film, and the coated glass article has a* chromaticity coordinates in the range of −

4.5 to 0 and b* chromaticity coordinates in the range of 0 to −

8, and a visible light transmittance in the range of 43 to 69% at a reference thickness of 0.223 inches (5.66 mm).

9. The coated glass article according to claim 8, wherein the glass substrate has a* chromaticity coordinates in the range of −

3 to +1 and a b* chromaticity coordinates in the range of −

2 to −

10 at a reference thickness of 0.223 inches (5.66 mm).

10. The coated glass article according to claim 4, wherein the coated article has a hemispherical emissivity of no greater than 0.05.

11. The coated glass article according to claim 10, wherein the coating is an infrared reflective coating comprising a first silver film over a first dielectric film, a second dielectric film over the first silver film, a second silver layer over the second dielectric film, a third dielectric film over the second silver film a third silver film over the third dielectric film and a fourth dielectric film over the third silver film, and the coated glass article has a* chromaticity coordinates in the range of −

6 to −

2 and b* chromaticity coordinates in the range of 2 to −

6, and a visible light transmittance in the range of 36 to 63% at a reference thickness of 0.223 inches (5.66 mm).

12. The coated glass article according to claim 11, wherein the glass substrate has a* chromaticity coordinates in the range of −

3 to +1 and b* chromaticity coordinates in the range of −

2 to −

10 at a reference thickness of 0.223 inches (5.66 mm).

13. The coated glass article according to claim 1, wherein the glass substrate is a first glass sheet and further comprising a second glass sheet laminated to the first sheet with the coating between the first and second glass sheets.

14. The coated glass article according to claim 11, wherein the glass substrate comprises a glass composition comprising a base glass portion and a glass colorant portion, wherein the base glass portion is a soda-lime-silica base portion, and the glass colorant portion comprising:

total iron, expressed as Fe₂O₃, in the range of 0.04 to 0.28 weight percent;

CoO in the range of 32 to 90 parts per million;

Se in the range of 1 to 5.5 parts per million;

ratio of CoO to Se, each expressed in parts per million, equal to or greater than 6, wherein the weight percent and the parts per million are based on the final glass composition.

15. The coated glass article according to claim 14, wherein the glass substrate, further comprising at least one colorant selected from Cr₂O₃, MnO₂, Nd₂O₃, NiO, TiO₂ and Er₂O₃.

16. The coated glass article according to claim 14, wherein the glass composition has a redox ratio in the range of 0.05 to 0.40.

17. The coated glass article according to claim 14, wherein the base glass composition comprises:

18. The coated glass article according to claim 4, wherein the redox ratio of the glass substrate is in the range of 0.10 to 0.30.

19. In an insulating unit of the type having a coated first glass sheet spaced a second glass sheet, with edges of the glass sheets sealed to provide a sealed space between the first and the second glass sheets, wherein the improvement comprises:

the coated glass sheet comprises a glass substrate comprising a base glass portion and a glass colorant portion, the glass colorant portion having colorants in selected amounts to provide the glass substrate with chromaticity coordinates of a* in the range of −

3.5 to +2.5 and b* in the range of −

1 to −

15, and a visible light transmittance of 40 to 80% at a reference thickness of 0.223 inches (5.66 mm); and

the coated glass sheet has chromaticity coordinates of a* in the range of −

7 to +2.0 and b* in the range of 3 to −

13, and a visible light transmittance of in the range of 26 to 75% at a reference thickness of 0.223 inches (5.66 mm), and a hemispherical emissivity of no greater than 0.25.

20. The insulating unit according to claim 19, wherein the second glass sheet is an uncoated second glass sheet, the first and the second glass sheets are spaced at a distance from one another in the range of 0.25 to 0.75 inches, the sealed space containing a gas, and the uncoated second glass sheet having chromaticity coordinates of a* in the range of −

2.3 to −

1.3 and b* in the range of −

2 to 0.4, and a visible light transmittance in the range of 87.5% to 89% at a reference thickness of 0.223 inches (5.66 mm); and

the insulating unit having visible light transmittance in the range of 26 to 67% and a solar heat gain coefficient of no greater than 0.50 at the coated first glass sheet and the uncoated second glass sheet reference thickness of 0.223 inches (5.66 mm).