Temperable three layer antireflective coating, coated article including temperable three layer antireflective coating, and/or method of making the same
First Claim
1. A coated article comprising:
- an antireflective coating supported by a major surface of a substrate, the substrate being heat treated together with the antireflective coating,wherein the antireflective coating comprises, in order moving away from the substrate;
a medium index layer comprising silicon oxynitride and having a index of refraction of from about 1.65 to 2.0 at 380 nm, 550 nm, and 780 nm wavelengths,a high index layer having an index of refraction of at least about 2.0 at 380 nm, 550 nm, and 780 nm wavelengths,a low index layer having an index of refraction of from about 1.4 to 1.6 at 380 nm, 550 nm, and 780 nm wavelengths,wherein the medium index layer has compressive residual stress after heat treatment; and
wherein the high index layer comprises an oxide of titanium, and has a thickness of from about 12 to 22 nm.
2 Assignments
0 Petitions
Accused Products
Abstract
A coated article includes a temperable antireflection (AR) coating that utilizes medium and low index (index of refraction “n”) layers having compressive residual stress in the AR coating. In certain example embodiments, the coating may include the following layers from the glass substrate outwardly: silicon oxynitride (SiOxNy) medium index layer/high index layer/low index layer. In certain example embodiments, depending on the chemical and optical properties of the high index layer and the substrate, the medium and low index layers of the AR coating are selected to cause a net compressive residual stress and thus optimize the overall performance of the antireflection coating when the coated article is tempered and/or heat-treated.
44 Citations
27 Claims
-
1. A coated article comprising:
-
an antireflective coating supported by a major surface of a substrate, the substrate being heat treated together with the antireflective coating, wherein the antireflective coating comprises, in order moving away from the substrate; a medium index layer comprising silicon oxynitride and having a index of refraction of from about 1.65 to 2.0 at 380 nm, 550 nm, and 780 nm wavelengths, a high index layer having an index of refraction of at least about 2.0 at 380 nm, 550 nm, and 780 nm wavelengths, a low index layer having an index of refraction of from about 1.4 to 1.6 at 380 nm, 550 nm, and 780 nm wavelengths, wherein the medium index layer has compressive residual stress after heat treatment; and wherein the high index layer comprises an oxide of titanium, and has a thickness of from about 12 to 22 nm. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14)
-
-
15. A coated article comprising:
-
an antireflective coating supported by a major surface of a substrate, the substrate being heat treated together with the antireflective coating, wherein the antireflective coating comprises, in order moving away from the substrate; a medium index layer comprising silicon oxynitride and having a index of refraction of from about 1.65 to 2.0 at 380 nm, 550 nm, and 780 nm wavelengths, a high index layer having an index of refraction of at least about 2.0 at 380 nm, 550 nm, and 780 nm wavelengths, a low index layer having an index of refraction of from about 1.4 to 1.6 at 380 nm, 550 nm, and 780 nm wavelengths, wherein the medium index layer has compressive residual stress after heat treatment; and wherein the medium index layer and the low index layer both have compressive residual stresses following heat treatment. - View Dependent Claims (16, 17)
-
-
18. A coated article comprising:
-
an antireflective coating supported by a major surface of a substrate, the substrate being heat treated together with the antireflective coating, wherein the antireflective coating comprises, in order moving away from the substrate; a medium index layer comprising silicon oxynitride and having a index of refraction of from about 1.65 to 2.0 at 380 nm, 550 nm, and 780 nm wavelengths, a high index layer having an index of refraction of at least about 2.0 at 380 nm, 550 nm, and 780 nm wavelengths, a low index layer having an index of refraction of from about 1.4 to 1.6 at 380 nm, 550 nm, and 780 nm wavelengths, wherein the medium index layer has compressive residual stress after heat treatment; wherein the substrate is a low-iron glass substrate; and wherein the high index layer has a tensile residual stress and a thickness of less than 25 nm.
-
-
19. A heat treatable coated article, comprising:
-
an antireflective coating supported by a major surface of a substrate, wherein the antireflective coating comprises, in order moving away from the substrate; a medium index silicon-inclusive layer having a index of refraction of 1.8 or less at 550 nm and 780 nm wavelengths and 2.0 or less at 380 nm, a high index layer having an index of refraction higher than that of the medium index layer at 380 nm, 550 nm, and 780 nm wavelengths, wherein the high index layer has a thickness no greater than 20 nm, and a low index layer having an index of refraction lower than that of the medium index layer at 380 nm, 550 nm, and 780 nm wavelengths, wherein the medium index layer and the low index layer have compressive residual stress, the high index layer has tensile residual stress, and the antireflective coating has a net compressive residual stress. - View Dependent Claims (20, 21, 22, 23, 24, 25, 26, 27)
-
Specification