Ultra thick bamboo-wood composite panel, ultra thick solid wood composite panel and manufacturing methods thereof

• US 8,747,987 B2
• Filed: 12/22/2009
• Issued: 06/10/2014
• Est. Priority Date: 12/24/2008
• Status: Expired due to Fees

• Current Assignee: Research Institute of Wood Industry Chinese Academy of Forestry
• Original Assignee: Research Institute of Wood Industry Chinese Academy of Forestry
• Inventors: Yu, Wenji, Yu, Yanglun, Zhou, Yue, Zhu, Rongxian, Ren, Dinghua
• Primary Examiner(s): O'HERN, BRENT T
• Application Number:
  US13/142,111
• Publication Number:
  US 20110274872A1
• Time in Patent Office: 1,631 Days
• Field of Search: 428/106, 428/98, 428/105, 144/352
• US Class Current: 428/106
• CPC Class Codes: B27D 1/04 to produce plywood or articles made therefrom; Plywood sheets making a layered veneer cutting block B27L5/00
• CPC Class Codes: B27D 1/06 Manufacture of central layers; Form of central layers see also B27M3/002 and B27M3/0026
• CPC Class Codes: B32B 21/14 comprising wood board or veneer
• CPC Class Codes: B32B 2307/50 having particular mechanical properties
• CPC Class Codes: B32B 2307/538 Roughness
• CPC Class Codes: B32B 2307/54 Yield strength; Tensile strength
• CPC Class Codes: B32B 2307/732 Dimensional properties
• CPC Class Codes: B32B 2607/00 Walls, panels
• CPC Class Codes: B32B 7/12 using interposed adhesives or interposed materials with bonding properties
• CPC Class Codes: Y10T 428/24 Structurally defined web or sheet [e.g., overall dimension, etc.]
• CPC Class Codes: Y10T 428/24058 including grain, strips, or filamentary elements in respective layers or components in angular relation
• CPC Class Codes: Y10T 428/24066 Wood grain
• CPC Class Codes: Y10T 428/24132 including grain, strips, or filamentary elements in different layers or components parallel
• CPC Class Codes: Y10T 428/24537 Parallel ribs and/or grooves

Abstract

A composite panel and its manufacture are described. Ultra-thick bamboo/wood and solid wood composite panels are comprised of core board, surface board and back board. The core board is composed of ultra-thick peeling veneers with thickness of 6 to 12 mm. Both surface board and back board are made of bamboo or wood. The core board comprises several layers of the ultra-thick veneers, and the veneers of contiguous layer are assembled with parallel structure. A glue layer is arranged between contiguous veneers; adhesive in the glue layer is aqueous macromolecule isocyanate adhesive. The ultra-thick veneers of the core layer are the veneers with stress degradation treatment, i.e., punctate or line segment cracks are formed along the grain of the veneer'"'"'s loose side in each layer.

Claims

1. An ultra-thick wood/bamboo composite panel, comprising core board, surface board and back board, wherein said core board is comprised of several ultra-thick peeling veneers, each veneer having a thickness of 6 to 12 mm;

both said surface board and said back board are made of bamboo;

veneers of contiguous layer in said core board are assembled with parallel structure or cross structure;

said ultra-thick veneers constituting the core board are veneers with stress degradation treatment, punctate or line segment cracks are formed along grain of the loose side of said veneer in each layer, and average length is in a range of 20 to 50 mm and average depth is from ¼

to ½

of veneer thickness for said cracks in the loose side of said veneer; and

a glue layer is arranged between adjacent veneers.

2. An ultra-thick wood/bamboo composite panel according to claim 1, wherein for said cracks in the loose side of said veneer, average width is in a range of 0.2 to 3 mm, and average distance between the cracks is from 5 to 50 mm.

3. An ultra-thick wood/bamboo composite panel according to claim 1, wherein total thickness of said wood/bamboo composite panel is in a range of 45 to 90 mm.

4. An ultra-thick wood/bamboo composite panel according to claim 1, wherein for said wood/bamboo composite panel, thickness ratio of the bamboo as surface board and back board to the wood is from 1:

10 to 2;

1.

5. An ultra-thick wood/bamboo composite panel according to claim 1, wherein said bamboo is bamboo scrimber with thickness of 5 to 20 mm, or glued laminated bamboo with thickness of 5 to 20 mm.

6. An ultra-thick wood/bamboo composite panel according to claim 1, wherein the glue layer between lamellae in said ultra-thick wood/bamboo composite panel is aqueous macromolecule isocyanate adhesive, and glue spread amount is in a range of 80 to 300 g/m².

7. An ultra-thick wood/bamboo composite panel according to claim 1, wherein the glue layer between lamellae in said ultra-thick wood/bamboo composite panel is resorcinol adhesive, and glue spread amount is in a range of 150 to 300 g/m².

8. A manufacturing method for ultra-thick wood/bamboo composite panel according to claim 1, comprising raw material preparation procedure, glue spreading procedure, assembling procedure, forming procedure and maintenance procedure,

(1) raw material preparation procedure

wherein the raw material preparation procedure includes preparation of bamboo, peeling of veneer, stress degradation treatment of veneer, and glue regulating, wherein the preparation of bamboo includes preparation of bamboo scrimber and preparation of glued laminated bamboo;

1.1 bamboo is made into bamboo scrimber or glued laminated bamboo to be surface board and back board;

1.2 log is peeled into ultra-thick veneers with thickness of 6 to 12 mm, punctate or line segment cracks are formed along grain of the loose side of said veneer in each layer by stress degradation using stress degradation machine, and average length is in a range of 20 to 50 mm and average depth is from ¼

to ½

of veneer thickness for said cracks in the loose side of said veneer, after drying treatment, moisture content of the veneer is in a range of 7 to 25%;

1.3 adhesive used is aqueous macromolecule isocyanate adhesive, comprising main agent and cross linking agent, the main agent is styrene-butadiene latex, vinyl acetate-ethylene copolymer emulsion or polyacrylic acid emulsion, and the cross linking agent is polymerized isocyanate;

amount of cross linking agent is from 5 to 20% of that of the main agent, after stirring uniformly, aqueous macromolecule isocyanate adhesive is formed;

or

adhesive used is resorcinol adhesive, comprising main agent and curing agent, the main agent is linear resorcinol resin containing alcohol, and the curing agent is polyformaldehyde;

amount of polyformaldehyde is 8 to 15% of that of main agent, after stirring uniformly, resorcinol adhesive is formed;

(2) glue spreading procedure

wherein aqueous macromolecule isocyanate adhesive or resorcinol adhesive is spread uniformly on a surface of the stress degraded wood veneer and on a surface of bamboo scrimber or glued laminated bamboo;

glue spread amount in each glue layer is from 80 to 300 g/m² for aqueous macromolecule isocyanate adhesive, and glue spread in each glue layer is from 150 to 300 g/m² for resorcinol adhesive;

(3) assembling procedure

wherein the bamboo scrimber or glued laminated bamboo and the stress degraded veneer are assembled with parallel structure or cross structure, several said stress degraded veneers are assembled together to form the core board, bamboo scrimber or glued laminated bamboo are placed on two sides of the core board so as to be used as surface board and back board, and then a slab is formed; and

(4) forming procedure

wherein said slab is sent to cold pressing machine to cold press, cold pressing pressure is in a range of 1 to 5 MPa, cold pressing time is in a range of 20 to 60 min, and cold pressing temperature is room temperature.

9. A manufacturing method for ultra-thick wood/bamboo composite panel according to claim 8, wherein a fifth procedure is arranged after the forming procedure:

(5) maintenance procedure

wherein said slab is stacked in an oven at a temperature of 60 to 120°

C. with a humidity of 60 to 98%, maintenance time is in a range of 1 to 5 h, and maintenance pressure is in a range of 0.6 to 2 MPa.

10. A solid wood composite panel made of ultra-thick veneers, comprising surface layer of two outer surfaces and core layer between the outer surfaces, and adhesive arranged between veneers in each layer;

wherein

said core layer is comprised of several ultra-thick veneers, each veneer having a thickness of 6 to 12 mm, and said surface layer is comprised of veneers with thickness of 0.2 to 1.5 mm; and

the ultra-thick veneers used in said core layer are veneers made by peeling of log, and punctate or line segment cracks are formed along grain of the loose side of said veneer in each layer, and average length is in a range of 20 to 50 mm and average depth is ⅙

to ½

of veneer thickness for said cracks in the loose side of said ultra-thick veneer used in said core layer.

11. A solid wood composite panel made of ultra-thick veneer according to claim 10, wherein for said cracks in the loose side of said ultra-thick veneer used in said core layer, average width is in a range of 0.2 to 3 mm and average distance between the cracks is 5 to 50 mm.

12. A solid wood composite panel made of ultra-thick veneer according to claim 10, wherein said core layer is composed of even-ply veneers, such as 2-ply, 4-ply, 6-ply, 8-ply, and so on, and the core layer is assembled with parallel structure or cross structure;

or

said core layer is composed of even-ply veneers, such as 2-ply, 4-ply, 6-ply, 8-ply, and so on, and the core board is assembled with parallel or cross structure;

a sub-surface layer, which is a balanced layer, is arranged between said core layer and said surface layer, the balanced layer is composed of veneers with thickness of 1 to 3 mm, and veneer of the sub-surface layer is arranged as vertical or interlaced to wood grain of veneers in said core board and said surface layer;

or

said core layer is composed of odd-ply veneer, such as 3-ply, 5-ply, 7-ply, and so on, and the core layer is assembled with parallel structure or cross structure;

or

said core layer is composed of odd-ply veneer, such as 3-ply, 5-ply, 7-ply, and so on, said core layer is assembled with parallel or cross structure;

a sub-surface layer, which is a balanced layer, is arranged between said core layer and said surface layer, said balanced layer is composed of veneers with thickness of 1 to 3 mm, and veneer of the sub-surface layer is arranged as vertical or interlaced to wood grain of veneer in said core layer and said surface layer.

13. A solid wood composite panel made of ultra-thick veneer according to claim 12, wherein two veneers with the loose side jointed relatively or one veneer in symmetrical centre of said core board are a middle core board, all the loose sides of veneers in each layer outside of the middle core board are toward the middle core board, and veneers are assembled symmetrically, with grains parallel to central two layers, or vertical or interlaced to central two layers.

14. A solid wood composite panel made of ultra-thick veneer according to claim 10, wherein said core layer is made of inferior wood selected from the group consisting of poplar, Chinese fir, cryptomeria, metasequoia and spruce;

and said surface layer is made of teak, dalbergia hupeana or keruing wood.

15. A solid wood composite panel made of ultra-thick veneer according to claim 12, wherein said sub-surface layer is composed of common veneers made of poplar, birch or eucalypt.

16. A manufacturing method for solid wood composite panel made of ultra-thick veneers according to claim 10, comprising the steps:

A. veneers manufacture

wherein wood for making core layer veneers, is peeled into ultra-thick veneers with thickness of 6 to 12 mm, said veneers are untwined in stress degradation equipment, punctate or line segment cracks being formed along grain in the loose side of said veneer, average length is in a range of 20 to 50 mm and average depth is ⅙

to ½

of veneer thickness for said cracks, then the veneers are used as veneers for core layer;

wood for making surface board, is peeled into veneers with thickness of 0.2 to 1.5 mm, then the veneers are used as decorative veneers for surface board;

B. drying

wherein the veneers are dried until moisture content is in a range of 8 to 15%;

C. glue spread

wherein double-sided sizing is carried out on the ultra-thick veneers of the core layer, and gluing is not on veneers of the surface layer;

D. assembling

wherein all said sizing ultra-thick veneers are assembled to form the core layer, and two thin veneers of the surface layer are assembled symmetrically on upper and lower surfaces of a slab as vertical or interlaced to wood grain of the core board; and

E. hot-pressing

the slab is hot pressed to become one flesh.

17. A manufacturing method for solid wood composite panel made of ultra-thick veneers according to claim 16, wherein for a sub-surface layer between said core layer and said surface layer, in the veneers manufacture procedure A, wood for making the sub-surface board is peeled into veneers with thickness of 1 to 3 mm;

in the drying procedure B, the veneers are also dried until moisture content is in a range of 8 to 15%;

in the glue spreading procedure C, the double-sided sizing is used;

then in the assembling procedure D, the veneers for the sub-surface layer are arranged between core layer veneers and surface layer veneers as wood grain vertical or interlaced to wood grain of the core layer and the surface layer.

18. A manufacturing method for solid wood composite panel made of ultra-thick veneer according to claim 16, wherein in the assembling procedure, said core layer is assembled as following:

two veneers with the loose sides jointed relatively or one veneer in symmetrical centre of said core board are a middle core board, all the loose sides of veneers in each layer outside of the middle core board are toward the middle core board, and veneers are assembled symmetrically with grains parallel to central two layers, or vertical or interlaced to central two layers.

19. A manufacturing method for solid wood composite panel made of ultra-thick veneer according to claim 16, wherein adhesive used is an urea-formaldehyde resin or melamine modified urea-formaldehyde resin, hot-pressing time is in a range of 0.5 to 1.6 min/mm, hot-pressing pressure is in a range of 0.7 to 2 MPa, hot-pressing temperature is in a range of 120 to 160°

C., and glue spread amount is in a range of 150 to 300 g/m²;

or

adhesive used is a phenolic-aldehyde adhesive, glue spread amount is in a range of 150 to 300 g/m², hot-pressing time is in a range of 0.5 to 2.0 min/mm, hot-pressing temperature is in a range of 130 to 180°

C., and hot-pressing pressure is in a range of 0.7 to 2.0 MPa;

or

adhesive used is isocyanate, glue spread amount is in a range of 20 to 50 g/m², hot-pressing time is in a range of 0.5 to 1.2 min/mm, hot-pressing temperature is in a range of 90 to 130°

C., and hot-pressing pressure is in a range of 0.7 to 2.0 MPa.