Method for in-situ manufacture of a lightweight fly ash based aggregate

• US 8,795,429 B2
• Filed: 09/14/2011
• Issued: 08/05/2014
• Est. Priority Date: 12/30/2010
• Status: Expired due to Fees

• Current Assignee: United States Gypsum Company (GEBR Knauf Verwaltungsgesellschaft KG)
• Original Assignee: United States Gypsum Company (GEBR Knauf Verwaltungsgesellschaft KG)
• Inventors: Perez-Pena, Marianela
• Primary Examiner(s): MARCANTONI, PAUL D
• Application Number:
  US13/232,128
• Publication Number:
  US 20120167804A1
• Time in Patent Office: 1,056 Days
• Field of Search: 106/772, 106/778
• US Class Current: 106/772
• CPC Class Codes: C04B 18/021 agglomerated by a mineral binder, e.g. cement
• CPC Class Codes: C04B 18/027 Lightweight materials
• CPC Class Codes: C04B 18/08 Flue dust , i.e. fly ash
• CPC Class Codes: C04B 18/146 Silica fume
• CPC Class Codes: C04B 22/143 Calcium-sulfate
• CPC Class Codes: C04B 24/06 containing hydroxy groups
• CPC Class Codes: C04B 38/10 by using foaming agents C04B38/02 takes precedenceor by using mechanical means, e.g. adding preformed foam
• CPC Class Codes: C04B 7/02 Portland cement
• CPC Class Codes: Y02W 30/91 Use of waste materials as fillers for mortars or concrete

Abstract

A method of making a rapid setting lightweight homogeneous foamed fly ash based cementitious aggregate composition with improved compressive strength for products such as panels is disclosed. The method mixes fly ash, alkali metal salt of citric acid, foaming agent for entraining air, optional foam stabilizing agent, a calcium sulfate such as stucco or gypsum, and water. Compositions are also disclosed which include mixtures of fly ash, particularly Class C fly ash alone or in mixtures with Class F fly ash, alkali metal salts of citric acid, foaming agents, a calcium sulfate such as calcium sulfate dihydrate or hemihydrate and an optional portland cement.

Claims

1. A method of making loose aggregate particles consisting of the steps of:

forming a mixture by mixing ingredients consisting essentially of;

water,

cementitious reactive powder consisting essentially of fly ash and a calcium sulfate selected from the group consisting of calcium sulfate hemihydrate, calcium sulfate dihydrate, and mixtures thereof, and optional silica fume,

an alkali metal salt of citric acid selected from the group consisting of sodium citrate, potassium citrate and mixtures thereof,

a foaming agent, and

optionally at least one or more member selected from the group consisting of secondary aggregate other than said loose aggregate, superplasticizer, set accelerating agents other than said alkali metal salt of citric acid, set retarding agents, shrinkage control agents, thickening agents, coloring agents, and internal curing agents, and

reacting the mixture in situ at a temperature of about 20°

C. to 41°

C. by mixing for about 3 to 6 minutes to form aggregate particles comprising hydration products of the fly ash and calcium sulfate in the mixture and crystalline hydration products of the fly ash and calcium sulfate which are also formed in situ and are interspersed within and between the aggregate particles to bind the aggregate particles, and

separating the aggregate particles as loose aggregate particles from the mixture.

2. The method of claim 1, wherein the wet density of the resulting mixture is about 40 to 65 pounds per cubic foot, wherein the mixture has no hydraulic cement, and said ingredients consisting essentially of said water, said cementitious reactive powder, said alkali metal salt of citric acid, and said foaming agent.

3. The method of claim 1, wherein the fly ash in the reactive powder comprises 88.5 to 100% class C fly ash, and wherein the mixture has a set time of about 4 to 6 minutes.

4. The method of claim 1, wherein the calcium sulfate is calcium sulfate dihydrate.

5. The method of claim 1, wherein the cementitious reactive powder is selected from the group consisting of class C fly ash and calcium sulfate hemihydrate or stucco, mixtures of class C and class F fly ash, calcium sulfate hemihydrate or stucco and/or Portland cement and mixtures of class F fly ash with class C fly ash and/or Portland cement and calcium sulfate hemihydrate or stucco.

6. The method of claim 1, wherein the wet density of the resulting mixture is about 46 to 51 pounds per cubic foot;

wherein the mixture has no hydraulic cement, wherein the ingredients consist of said water, said cementitious reactive powder, said alkali metal salt, said foaming agent, and optional superplasticizer.

7. The method of claim 1, wherein the alkali metal salt of citric acid is in an amount of about 1.5 to 6 wt. % based on the weight of the cementitious reactive powder.

8. The method of claim 1, wherein the cementitious reactive powder comprises 60 to 95 wt. % fly ash and 5 to 40 wt. % calcium sulfate selected from the group consisting of calcium sulfate hemihydrate, calcium sulfate dihydrate, and mixtures thereof.

9. The method of claim 1, further including setting the cementitious mixture comprising the aggregate particles in situ and recovering the aggregate particles from the set cementitious mixture by a suitable recovery process to separate the aggregate particles from the set mixture.

10. The method of claim 1, wherein the cementitious reactive powder includes the silica fume and has no Portland cement and no calcium aluminate cement, wherein the mixture has no other hydraulic cement, wherein the ingredients consist of said water, said cementitious reactive powder, said alkali metal salt, and said foaming agent, and optionally a member at least one member selected from the group consisting of superplasticizers, set accelerating agents other than said alkali metal salt of citric acid, set retarding agents, shrinkage control agents, thickening agents, coloring agents, and internal curing agents.

11. The method of claim 1, wherein the cementitious reactive powder and water are present in a weight ratio of about 0.200 to 0.287:

1 part by weight water to reactive powder.

12. The method of claim 1, wherein the cementitious reactive powder and water are present in a weight ratio of about 0.22-0.287:

1 part by weight water to reactive powder.

13. The method of claim 1, for forming a lightweight cementitious aggregate:

wherein the cementitious reactive powder consists of 60 to 95 wt. % fly ash, and

wherein the ratio of water to cementitious reactive powder solids in the mixture is about 0.17 to 0.35;

1.

14. The method of claim 13, wherein the cementitious reactive powder consists of fly ash which is 88.5 to 100 wt. % Class C fly ash, calcium sulfate, optional silica fume and no Portland cement and no other hydraulic cement.

15. The method of claim 13, wherein the amount of alkali metal salt of citric acid mixed into the mixture is about 1.5 to 6.0 wt. %, based upon the weight of cementitious powder.

16. The method of claim 13, wherein the cementitious reactive powder is selected from the group consisting of class C fly ash and calcium sulfate hemihydrate or stucco, mixtures of class C and class F fly ash and calcium sulfate hemihydrate or stucco;

and mixtures of class F fly ash with class C fly ash and/or Portland cement and calcium sulfate hemihydrate stucco.

17. The method of claim 1, wherein the fly ash of the cementitious reactive powder consists of 30-46 wt % class F fly ash and 54-70 wt % class C fly ash and the mixture has no portland cement and no other hydraulic cement.

18. The method of claim 1, wherein the cementitious reactive powder consists of 46 to 60 wt. % Class F fly ash, 10 to 32 wt. % Class C fly ash, and 10-29 wt % calcium sulfate hemihydrate or stucco and wherein the weight ratio of water to the total weight of fly ash and calcium sulphate is less than about 0.33 to 0.37.

19. The method of claim 1, wherein the aggregate particles consist of a homogeneous mixture of spherical shaped particles of the reaction of the fly ash and calcium sulfate having a diameter of less than about 1 mm formed in situ and the crystalline hydration product of said fly ash and calcium sulfate, which is also formed in situ and interspersed in and between the particles and binding said particles together in the aggregate.

20. A method of making loose aggregate particles consisting of:

forming a mixture by mixing ingredients consisting of;

water,

cementitious reactive powder consisting of fly ash, optional hydraulic cement, optional non-fly ash mineral additive, optional added lime, a calcium sulfate selected from the group consisting of calcium sulfate hemihydrate, calcium sulfate dihydrate, and mixtures thereof, and optional silica fume,

an alkali metal salt of citric acid selected from the group consisting of sodium citrate, potassium citrate and mixtures thereof,

a foaming agent, and

optionally at least one or more member selected from the group consisting of secondary aggregate other than said loose aggregate, superplasticizer, set accelerating agents other than said alkali metal salt of citric acid, set retarding agents, shrinkage control agents, thickening agents, coloring agents, and internal curing agents, and

reacting the mixture in situ at a temperature of about 20°

C. to 41°

C. by mixing for about 3 to 6 minutes to form aggregate particles comprising hydration products of the fly ash and calcium sulfate in the mixture and crystalline hydration products of the fly ash and calcium sulfate which are also formed in situ and are interspersed within and between the aggregate particles to bind the aggregate particles, and

separating the aggregate particles as loose aggregate particles from the mixture.