Method of adopting inorganic seriflux mixture for applicating coating contg aluminium

Method of adopting inorganic seriflux mixture for applicating coating contg aluminium

  • CN 100,392,150 C
  • Filed: 09/05/2001
  • Issued: 06/04/2008
  • Est. Priority Date: 09/06/2000
  • Status: Active Grant
First Claim
Patent Images

1. coating method, comprising the following step:

  • Goods with surface to be coated (36) are provided;

    Preparation coating slurries, it comprises the mixture of following ingredients;

    Carrier components, it comprises water and inorganic gel agent, wherein first machine jelling agent is preferably about 1%-6 weight % of water and inorganic gel agent gross weight and is selected from HECTABRITE DP and POLARGEL NF and their mixture;

    The aluminium source, described aluminium source is selected from aluminium, chromium-aluminium alloy, cobalt-aluminium alloy, Ti-Al alloy, iron-aluminium alloy, aluminium-vanadium alloy, aluminum-manganese alloy and their mixture;

    WithDivided oxide powder, described divided oxide powder is selected from aluminum oxide, yttrium oxide, zirconium white, chromic oxide and hafnium oxide and their mixture;

    The coating slurries are applied on the product surface (36);

    ThenCoating slurries on the dried product surface (36) are removed moisture wherein;

    ThenHeat the product surface (36) that exsiccant coating slurries are arranged on it, to make and product surface (36) bonded aluminum cladding.