A kind of fenestrated membrane and the resistance to spread coated paint of protective membrane ultraviolet photo-curing and preparation method thereof

A kind of fenestrated membrane and the resistance to spread coated paint of protective membrane ultraviolet photo-curing and preparation method thereof

  • CN 102,260,453 B
  • Filed: 12/14/2010
  • Issued: 08/19/2015
  • Est. Priority Date: 12/14/2010
  • Status: Active Grant
First Claim
Patent Images

1. the resistance to spread coated paint of ultraviolet photo-curing, it is made up of following material composition:

  • The vinylformic acid 2-hydroxyl ethyl ester of 3 weight parts, 5 parts by weight of acrylic acid N, N DMAA, the glycerine three hydroxypropyl ether triacrylate of 5 weight parts, the pentaerythritol tetracrylate of 5 weight parts, the acrylic acid modified polyurethane of 40 weight parts, phenylbenzene-(2,4,6-trimethylbenzoyl) oxygen phosphorus of 5 weight parts, the Siloxane-Oxyalkylene Copolymers of 0.05 weight part, the acrylic acid series flow agent of 0.05 weight part;

    Or,The vinylformic acid 2-hydroxyl ethyl ester of 6 weight parts, 2 weight part 2-phenoxyethyl acrylate, the pentaerythritol tetracrylate of 10 weight parts, the 1,6 hexanediol diacrylate of 13 weight parts, the unsaturated polyester modified polyurethane of 40 weight parts, the dimethoxybenzoin of 6 weight parts, the polyester-modified polysiloxanes of 0.05 weight part, the silicone based flow agent of 0.05 weight part;

    Or,The vinylformic acid 2-hydroxyl ethyl ester of 7 weight parts, the Propylene glycol monoacrylate of 2 weight parts, the pentaerythritol triacrylate of 9 weight parts, the 2-[[2 of 20 weight parts, 2-two [[(1-oxo-2-propenyl] methyl] butoxy] methyl]-2-ethyl-1,3-propane two base-2-acrylate, the acrylic acid modified polyurethane of 30 weight parts, the 1-hydroxycyclohexylphenylketone of 7 weight parts, the polyether-polyester modified polyorganosiloxane of 0.05 weight part, the silicone based flow agent of 0.05 weight part;

    Or,The glycerine three hydroxypropyl ether triacrylate of the 2-phenoxyethyl acrylate of 7 weight parts, the Propylene glycol monoacrylate of 2 weight parts, 9 weight parts, the 2-[[2 of 6 weight parts;

    2-two [[(1-oxo-2-propenyl] methyl] butoxy] methyl]-2-ethyl-1,3-propane two base-2-acrylate, the acrylic acid modified polyurethane of 25 weight parts, the 4-benzoyl-4'"'"'-methyl-diphenyl sulfide of 7 weight parts, the polyester-modified polysiloxanes of 0.05 weight part, the silicone based flow agent of 0.05 weight part.

View all claims
    ×
    ×