A kind of antiflaming floor and production technology thereof

A kind of antiflaming floor and production technology thereof

  • CN 102,777,014 B
  • Filed: 08/16/2012
  • Issued: 04/27/2016
  • Est. Priority Date: 08/16/2012
  • Status: Active Grant
First Claim
Patent Images

1. an antiflaming floor, is characterized in that:

  • comprise substrate (1), apply one deck 10 ~ 25g/cm on the surface of substrate 2inflaming retarding finish paint, coating inflaming retarding finish paint after and carry out ultraviolet curing, ultraviolet curing be by Ultraviolet radiation inflaming retarding finish paint surface, solidification energy is 200 ~ 250mj/cm 2, hardening time is 3 ~ 5 seconds;

    The paint that described inflaming retarding finish paint layer (2) adopts is JSRF01 paint;

    The below of described inflaming retarding finish paint layer (2) is also provided with 7 road coatings, the second inflaming retarding finish paint layer (3) from top to bottom respectively, fire-retardant prime coat (4), the second fire-retardant prime coat (5), sanding prime coat (6), elastic bottom enamelled coating (7), putty (8) and water-based adhesive agent (9);

    Described;

    (1) the paint that, inflaming retarding finish paint layer (2) and the second inflaming retarding finish paint layer (3) adopt is JSRF01 paint;

    (2) the paint that, fire-retardant prime coat (4) and the second fire-retardant prime coat (5) adopt is JSRF02 paint;

    (3) the paint that, sanding prime coat (6) adopts is 128058511 paint;

    (4) what, putty (8) adopted is 208068511 putty;

    (5) what, water-based adhesive agent (9) adopted is 108010511 water-based adhesive agents;

    The production technology of above-mentioned antiflaming floor, also comprises 7 road japanning operations before coating inflaming retarding finish paint, has following japanning operation in order successively;

    (1), apply 20g/cm 2water-based adhesive agent, and carry out infrared heating, drying, temperature 100 DEG C, time 10s;

    (2), apply 25g/cm 2putty, and carry out ultraviolet light polymerization, solidification energy 200mj/cm 2, hardening time is 4 seconds;

    (3), apply 35g/cm 2elastic primer, and carry out semi-solid preparation, solidification energy 100mj/cm 2, hardening time is 3 seconds;

    (4), apply 20g/cm 2sanding priming paint, and carry out all solidstate, solidification energy 220mj/cm 2, hardening time is 4 seconds;

    (5), apply 35g/cm 2fire-retardant priming paint, and carry out all solidstate, solidification energy 200mj/cm 2, hardening time is 4 seconds;

    (6), apply 30g/cm 2fire-retardant priming paint, and carry out all solidstate, solidification energy 200mj/cm 2, hardening time is 3 seconds;

    (7), apply 15g/cm 2inflaming retarding finish paint, and carry out all solidstate, solidification energy 200mj/cm 2, hardening time is 4 seconds.

View all claims
    ×
    ×