Making process of peony porcelain combining embossing, three-dimensional flower modeling and colored drawing

Making process of peony porcelain combining embossing, three-dimensional flower modeling and colored drawing

CN
  • CN 103,193,468 A
  • Filed: 04/09/2013
  • Published: 07/10/2013
  • Est. Priority Date: 04/09/2013
  • Status: Active Application
First Claim
Patent Images

1. the manufacture craft of the tree peony porcelain that combines with colored drawing of an embossment, the moulding of three-dimensional flower, comprise with the china clay and the water that prepare and be mixed and made into base substrate, put into the step of kiln biscuiting after drying, glazing on the base substrate of biscuiting, and put into the step that kiln forms by a firing, and make flower and the step of branches and leaves with the white porcelain mud for preparing, and it is characterized in that:

  • put into kiln after the first glazing of the flower that white porcelain mud is made and branches and leaves and fire, standby;

    With olibanum oil pigment is in harmonious proportion, draws out the lines of pattern according to detail of design at the base substrate that bakes, dry the back and under 800 ℃

    temperature, fired 2-10 hours, carry out colored drawing with pigment according to drawing the pattern of getting well on the base substrate afterwards;

    Respectively the flower and the branches and leaves that bake are painted with the pigment that mediation is good, the base substrate that colored drawing is good and the flower of last lechery and branches and leaves are put into kiln respectively and are carried out decoration firing, after decoration firing finishes, coat low-temperature glaze at flower and branches and leaves bottom, be placed on the base substrate according to layout then, put into kiln after drying in the air 2-3 hours and under 600-800 ℃

    temperature, fire and namely made product in 8-12 hour;

    Used pigment comprises red pigment, yellow ultramarine and veridian, wherein, the preparation method of red pigment is;

    at 900 ℃

    -1000 ℃

    temperature lower calcination, take out cooling back crushing screening after adopting 56-60wt% red lead, 20-22wt% boric acid, 1-2wt% ferric oxide, 10-14wt% quartz, 4-8wt% zinc oxide and 1-2wt% weisspiessglanz to mix;

    The preparation method of yellow ultramarine is;

    adopt 55-60wt% red lead, 8-10wt% boric acid, 3-5wt% zinc oxide, 10-12wt% quartz, 8-10wt% borax, 4-5wt% ferric oxide and 6-8wt% weisspiessglanz to mix the back at 900 ℃

    -1000 ℃

    temperature lower calcination, take out the cooling back and add toner, mix grinding and sieving;

    The preparation method of veridian is;

    adopt 60-62wt% red lead, 28-30wt% boric acid and 8-10wt% quartz at 900 ℃

    -1000 ℃

    temperature lower calcination, take out the cooling back and mixes with toner and aluminum oxide and put into 750 ℃

    -850 ℃

    again after the calcining, taking-up is cooled off, crushing screening;

    Wherein the add-on of aluminum oxide is 2-5% of veridian gross weight;

    Described embossment adopts cast, paste or the method for engraving is produced on the base substrate, perhaps in the colored drawing process on base substrate according to the embossing pattern full-filling glass white of design, and after decoration firing, make.

View all claims
    ×
    ×