Form the flexible glass-polymeric layer stack method for retaining shape

Form the flexible glass-polymeric layer stack method for retaining shape

  • CN 105,121,156 B
  • Filed: 02/24/2014
  • Issued: 10/15/2019
  • Est. Priority Date: 02/26/2013
  • Status: Active Grant
First Claim
Patent Images

1. a kind of formation flexible glass-polymer laminate method, which comprisesPolymeric layer is heated to the temperature promoted, the temperature of the promotion is greater than 20 DEG C and is less than adjacent with the polymeric layerThe thickness of the operating temperature of flexible glass substrate, the flexible glass substrate is no more than 0.3mm;

  • The polymeric layer and the flexible glass substrate is laminated, at the same the promotion at a temperature of make the flexible glassGlass substrate and the polymeric layer shape;

    AndThe polymeric layer is cooled to the temperature lower than the promotion, so that the intensity of the polymeric layer and rigidity maintain instituteState flexible glass-polymer laminate non-planar form;

    Wherein, the step of heating the polymeric layer it carries out making the polymeric layer and the flexible glass duringThe step of substrate is laminated.

View all claims
    ×
    ×