Laminated metal sheet for can lid excelling in appearance after retorting

• US 20070031688A1
• Filed: 11/30/2004
• Published: 02/08/2007
• Est. Priority Date: 12/01/2003
• Status: Abandoned Application

• Current Assignee: JFE Steel Corporation (JFE Holdings Incorporated)
• Original Assignee: JFE Steel Corporation (JFE Holdings Incorporated)
• Inventors: Iwasa, Hiroki, Kubo, Hiroshi, Suzuki, Takeshi
• Application Number:
  US10/580,122
• Publication Number:
  US 20070031688A1
• Time in Patent Office: Days
• US Class Current: 428/458
• CPC Class Codes: B32B 15/08 of synthetic resin
• CPC Class Codes: B32B 15/09 comprising polyesters
• CPC Class Codes: B32B 2250/02 2 layers
• CPC Class Codes: B32B 2307/702 Amorphous
• CPC Class Codes: B32B 2307/704 Crystalline
• CPC Class Codes: B32B 2439/66 Cans, tins
• CPC Class Codes: B32B 2439/70 Food packaging
• CPC Class Codes: B32B 27/36 comprising polyesters
• CPC Class Codes: Y10T 428/31681 Next to polyester, polyamide or polyimide [e.g., alkyd, glue, or nylon, etc.]

Abstract

The laminated metal sheet for can end is formed by laminating polyester film on both sides thereof, thus providing excellent appearance after retorting. The polyester film laminated to a side to become outer face of the formed can end has (1) half-time of crystallization of the resin of amorphous polyester layer formed near the interface between the polyester film and the metal sheet of 40 seconds or smaller at 130° C., (2) thickness of the amorphous polyester layer from 0.5 to 8 μm, (3) water vapor transmissivity of the polyester film of 100 g/m²/24 hr or smaller. The amorphous polyester layer resin is preferably a polyester composition prepared by formulating a polyester (I) (30 to 60% by weight) composed mainly of ethylene terephthalate as the main repeating unit, and a polyester (II) (40 to 70% by weight) composed mainly of butylene terephthalate as the main repeating unit.

Claims

1. A laminated metal sheet for can end comprising a metal sheet and a polyester film being laminated on the metal sheet, wherein the polyester film has an amorphous polyester layer having a thickness in a range from 0.5 to 8 μ

m, the amorphous polyester layer has a half-time of crystallization of 40 seconds or smaller at 130°

C., and the polyester film has a water vapor transmissivity of 100 g/m2/24 hr or smaller.

2. The laminated metal sheet for can end according to claim 1, wherein the amorphous polyester layer resin is a polyester composition prepared by formulating a polyester (I) composed of ethylene terephthalate as a main repeating unit, and a polyester (II) composed of butylene terephthalate as a main repeating unit, while the percentage of the polyester (I) is in a range from 30 to 60% by weight, and the percentage of the polyester (II) is in a range from 40 to 70% by weight.

3. The laminated metal sheet for can end according to claim 1, wherein the polyester film being laminated on the metal sheet on a side to become outer face of the formed end has a thickness of 10 μ

m or larger, and the total thickness of the polyester films being laminated on the metal sheet on both sides thereof to become outer face and inner face of the formed end is 60 μ

m or smaller.

4. The laminated metal sheet for can end according to claim 2, wherein the polyester film being laminated on the metal sheet on a side to become outer face of the formed end has a thickness of 10 μ

m or larger, and the total thickness of the polyester films being laminated on the metal sheet on both sides thereof to become outer face and inner face of the formed end is 60 μ

m or smaller.