LOW REFLECTIVITY ARTICLES AND METHODS THEREOF

• US 20150064405A1
• Filed: 10/18/2013
• Published: 03/05/2015
• Est. Priority Date: 04/20/2011
• Status: Abandoned Application

• Current Assignee: Corning Incorporated
• Original Assignee: Corning Incorporated
• Inventors: Koch, Karl William III, Kosik Williams, Ellen Marie
• Application Number:
  US14/057,638
• Publication Number:
  US 20150064405A1
• Time in Patent Office: Days
• US Class Current: 428/147
• CPC Class Codes: G02B 1/118 having sub-optical wavelength surface structures designed to provide an enhanced transmittance, e.g. moth-eye structures
• CPC Class Codes: Y10T 428/24372 Particulate matter
• CPC Class Codes: Y10T 428/24405 Polymer or resin [e.g., natural or synthetic rubber, etc.]
• CPC Class Codes: Y10T 428/24421 Silicon containing

Abstract

An anti-reflective article, including:

• • a substrate;
  • an integral binder region on at least a portion of the surface of the substrate; and
  • a nanoparticulate monolayer partially embedded in the integral binder region, as defined herein. The integral binder can be comprised of the same or different material as the substrate material. Methods of making and using the article are also disclosed.

Claims

1. An anti-reflective article, comprising:

a substrate;

an integral binder region on at least a portion of the surface of the substrate; and

a nanoparticulate monolayer partially embedded in the integral binder region, wherein the ratio of the thickness of the integral binder region (g) to the thickness or diameter (D) of the nanoparticulate monolayer (g;

D) is from 1;

50 to 3;

5.

2. The article of claim 1 wherein the substrate, the integral binder region, and the nanoparticulates of the nanoparticulate monolayer are each independently selected from at least one of a glass, a polymer, a ceramic, a composite, or a combination thereof.

3. The article of claim 1 wherein the partially embedded nanoparticulate monolayer comprises nanoparticles having an average diameter (D) of from 50 nm to about 300 nm.

4. The article of claim 1 wherein the integral binder region compromises the surface of the substrate having nanoparticles partially embedded into the surface of the substrate at an immersion depth (g) of from 1 nm to about 150 nm, and the nanoparticulate monolayer comprises nanoparticles having an average diameter (D) of from 50 nm to about 300 nm.

5. The article of claim 1 wherein the nanoparticles of the nanoparticulate monolayer comprise spheres of silica having an average diameter (D) less than at least one wavelength of visible light.

6. The article of claim 1 wherein the nanoparticulate monolayer has a plurality of unparticulated voids or areas of at least from 0.1 to 1 square microns.

7. The article of claim 1 wherein the nanoparticulate monolayer is comprised of sub-wavelength spherical silica particles.

8. A method of making the article of claim 1, comprising:

applying a monolayer of nanoparticulates to the integral binder region comprising at least one transiently softened surface of the substrate.

9. The method of claim 8 wherein applying the monolayer of nanoparticulates to the at least one transiently softened surface of surface of the substrate is accomplished by dip coating the substrate having the transiently softened surface into a mixture of the nanoparticulates.

10. The method of claim 8 wherein the at least one transiently softened surface of the substrate is accomplished before applying the monolayer of nanoparticulates to the surface of the substrate, and the applied nanoparticulates partially sink into the surface of the transiently softened substrate.

11. The method of claim 8 wherein the at least one transiently softened surface of the substrate is accomplished after applying the monolayer of nanoparticulates to the surface of the substrate, and the applied nanoparticulates partially sink into the surface of the transiently softened substrate.

12. The method of claim 8 wherein the monolayer of nanoparticulates is comprised of sub-wavelength spherical particles.

13. The method of claim 12 wherein the sub-wavelength spherical particles are comprised of at least one metal oxide.

14. The method of claim 13 wherein the at least one metal oxide is comprised of silica.

15. The method of claim 8 further comprising strengthening the substrate by ion-exchange before, after, or both before and after, applying the monolayer of nanoparticulates to the at least one transiently softened surface of surface of the substrate.