Method for preparing the matte anti-fingerprint stainless steel decorative plate
First Claim
1. A method for preparing a matte anti-fingerprint stainless steel decorative plate, comprising:
- 1) selecting a polymer coating material, wherein the polymer coating material is formed by mixing the following ingredients in weight ratio;
a film forming material, comprising 30-50 parts of acrylate composite resin, 5-20 parts of amino resin, and 5-15 parts of epoxy resin;
an inorganic nano-filler, in 1-5 parts;
a solvent, in 40-50 parts;
an auxiliary agent, in 10-20 parts;
1-8 parts of a matting agent; and
1-8 parts of an anti-settling agent;
wherein the polymer coating material has a PH value at about 4.8 to ensure film uniformity;
2) performing a spray coating using the polymer coating material to form a coating film, wherein the coating film has a thickness of 1.5-2.5 μ
m, and a precision of the atomization air pressure of a spray gun is controlled at ±
0.1 bar during the spray coating; and
drying the coating to obtain a finished product.
1 Assignment
0 Petitions
Accused Products
Abstract
The present invention provides a method for preparing a matte anti-fingerprint stainless steel decorative plate. The method comprises the steps of: 1) selecting a polymer coating material, wherein the polymer coating material is formed by mixing a film forming material, an inorganic nano-filler, a solvent and an auxiliary agent, wherein the film forming material comprises the following ingredients based on the weight ratio: 30-50 parts of acrylate composite resin, 5-20 parts of amino resin, and 5-15 parts of epoxy resin; and 1-8 parts of a matting agent and 1-8 parts of an anti-settling agent are added; and 2) performing a spray coating using the polymer coating material, wherein a coating film has a thickness of 1.5-2.5 μm, the precision of the atomization air pressure of a spray gun is controlled at ±0.1 bar during spray coating, and the coating is dried to obtain a finished product and then a matte anti-fingerprint stainless steel decorative plate which has a high-standard matte and anti-fingerprint index is prepared.
5 Citations
3 Claims
-
1. A method for preparing a matte anti-fingerprint stainless steel decorative plate, comprising:
-
1) selecting a polymer coating material, wherein the polymer coating material is formed by mixing the following ingredients in weight ratio; a film forming material, comprising 30-50 parts of acrylate composite resin, 5-20 parts of amino resin, and 5-15 parts of epoxy resin; an inorganic nano-filler, in 1-5 parts; a solvent, in 40-50 parts; an auxiliary agent, in 10-20 parts; 1-8 parts of a matting agent; and 1-8 parts of an anti-settling agent; wherein the polymer coating material has a PH value at about 4.8 to ensure film uniformity; 2) performing a spray coating using the polymer coating material to form a coating film, wherein the coating film has a thickness of 1.5-2.5 μ
m, and a precision of the atomization air pressure of a spray gun is controlled at ±
0.1 bar during the spray coating; anddrying the coating to obtain a finished product. - View Dependent Claims (2, 3)
-
Specification